Table 2 Comparison of water sorption and solubility (µg/mm3) between the study groups

From: Effect of thermocycling on surface topography and fracture toughness of milled and additively manufactured denture base materials: an in-vitro study

 

Milled (n = 10)

3D-printed (n = 10)

P value

Median (IQR)

Min - Max

Median (IQR)

Min – Max

Wsp 84 h

3.98 (0.99)

3.98–7.96

11.94 (4.97)

3.98–19.89

0.003*

Wsp after thermocycling

0.00 (7.96)

-3.98–19.89

1.99 (12.93)

-11.94–11.94

0.562

P value

0.154

0.020*

 

Wsl

-5.97 (23.87)

-15.92–11.94

-3.98 (11.94)

-15.92–3.98

0.759

  1. *Statistically significant difference at P < .05