Material | Section | Sintering temperature | F | P | ||||
---|---|---|---|---|---|---|---|---|
H1 | H2 | R | L2 | L1 | ||||
UG | Cervical | 26.91 ± 0.66 | 26.65 ± 0.36 | 26.82 ± 0.75B | 27.07 ± 0.85 | 26.60 ± 0.32 | 0.947 | 0.446 |
Body | 27.80 ± 0.48 | 27.95 ± 0.26 | 27.76 ± 0.68A | 28.39 ± 0.90 | 27.93 ± 0.52 | 1.678 | 0.172 | |
Incisal | 27.93 ± 0.63b | 28.42 ± 0.52b | 28.42 ± 0.64A,b | 29.62 ± 0.63a | 28.55 ± 0.61b | 10.584 | < 0.001 | |
UM | Cervical | 31.44 ± 0.49a | 31.44 ± 0.52a | 31.39 ± 0.74A,a | 30.45 ± 0.76b | 25.09 ± 1.01c | 142.966 | < 0.001 |
Body | 31.94 ± 0.52a | 31.60 ± 0.62a | 31.33 ± 0.56A,a | 30.38 ± 0.80b | 24.97 ± 0.87c | 177.074 | < 0.001 | |
Incisal | 31.81 ± 0.71a | 31.22 ± 0.77a,b | 30.51 ± 0.76B,b,c | 29.75 ± 0.79c | 23.13 ± 0.78d | 213.791 | < 0.001 | |
CX | Cervical | 29.48 ± 0.95a | 28.63 ± 0.85a,b | 28.46 ± 0.95A,a,b | 29.00 ± 1.09a,b | 28.15 ± 0.80b | 3.020 | 0.027 |
Body | 29.43 ± 0.90a | 28.28 ± 0.86b | 28.04 ± 0.77A,b | 28.34 ± 0.68b | 27.82 ± 0.80b | 5.953 | 0.001 | |
Incisal | 28.10 ± 0.72a | 26.51 ± 0.94c | 26.82 ± 0.59B,b | 26.81 ± 0.98b | 25.67 ± 1.08c | 9.888 | < 0.001 | |
LE | Cervical | 22.02 ± 1.06c | 24.68 ± 0.93b | 26.53 ± 0.43A,a | 26.87 ± 0.62a | 26.46 ± 0.60a | 70.769 | < 0.001 |
Body | 21.30 ± 0.97c | 23.65 ± 0.71b | 25.85 ± 0.47A,a | 26.48 ± 0.67a | 26.17 ± 0.51a | 102.171 | < 0.001 | |
Incisal | 20.34 ± 0.94d | 22.92 ± 0.76c | 24.40 ± 0.99B,b | 25.44 ± 0.45a | 24.84 ± 0.67a,b | 67.390 | < 0.001 |