Influence of surface treatment on repair bond strength of CAD/CAM long-term provisional restorative materials: an in vitro study

Abstract

Background

The surface treatment to improve the repair bond strength may vary because CAD/CAM provisional restoration polymers exhibit a variety of microstructures. This study was conducted to evaluate the effect of surface treatments on the repairability of three different CAD/CAM polymers for long-term provisional restorations.

Methods

Thirty specimens from each provisional restorative materials (CAD-Temp, Everest C-Temp, and PEEK) were divided into three groups: C: surfaces received no treatment; SB: surfaces were airborne particle abraded with 50 μm aluminum oxide; SB-T: surfaces received the same conditions as group SB in addition to thermocycling before and after treatment. Primer and nanohybrid repair resin composite were applied to the prepared CAD /CAM surfaces. The shear bond strength and the mode of failure were assessed. ANOVA and Tukey’s significant difference tests were used to evaluate the data.

Results

The SB group had significantly higher repair SBS values (p < .001) compared to the other groups (C and SB-T). Everest C-Temp significantly recorded the highest repair SBS (17.84 ± 0.19 MPa) in group SB, while the lowest repair SBS values (5.51 ± 1.14 MPa) for CAD-Temp were recorded in group C. PEEK significantly recorded the second highest repair SBS (15.96 ± 0.18) in the SB group.

Conclusions

Everest C-Temp had the highest repair SBS after an airborne abrasion particle. Thermocycling had no significant effect on the repair SBS for PEEK. Everest C-Temp and PEEK are recommended as long-term durable provisional materials for clinical use.

Peer Review reports

Introduction

There are many prefabricated polymer-based CAD/CAM materials in the market that can be used to fabricate provisional restorations. To improve material properties beyond conventional polymerization, prefabricated polymer blanks are industrially polymerized under standardized conditions at high temperature and pressure. Due to the increased fracture strength, better stress distribution, and less abrasion of the opposing enamel, these materials are more versatile [1,2,3].

Long-term provisional prostheses may present new therapeutic possibilities for maxillofacial rehabilitation, implant-supported treatments, and periodontal therapy [4,5,6]. Clinicians should consider the type of materials [7,8,9], simplicity of processing and bonding [10,11,12], mechanical properties, and oral environmental conditions [13] when choosing long-term provisional restorative materials. Although these restorations seem highly promising from a mechanical point of view, a resin composite veneering material is required for aesthetic reasons and their bonding durability in oral environments [14,15,16]. The durability of these CAD /CAM restorative polymers can be compromised by technical complications such as chipping, bond failure, and wear. These complications may lead to clinical failures and the need for additional operative treatment [12, 14].

When a fractured restoration is veneered with resin composite, the size and nature of the defect must be considered when the dentist decides whether to repair or replace the restoration [16]. The concept of repair is part of the philosophy of minimally invasive dentistry, which is based on the preservation of tooth structure and aims to avoid repeated cycles of restoration [17].

The repair requires special surface treatment because the interfacial adhesion between the new resin layers and the restoration degrades over time [18, 19]. Airborne-particle abrasion is a type of surface treatment to increase the surface area and wettability of the material, resulting in intimate adaptation of the resin/restoration interface and increased the repair bond strength. Because CAD/CAM interim restoration polymers demonstrate varied microstructures, the response to different surface treatments to enhance their repair bond strength may also vary [11, 12, 14]. Furthermore, there is scarce information available on the repairability of long-term provisional CAD/CAM restorations. As a result, the current study investigated the effect of surface treatments on the repairability of three different CAD /CAM polymers for long-term provisional restorations. The null hypotheses tested were that (1) there would be no significant difference among repair bond strength of the three different CAD/CAM materials, (2) the airborne particle abrasion does not affect repair bond strength, and (3) thermocycling does not affect repair bond strength.

Materials and methods

In this study, three types of CAD/CAM polymers for long term interim restorations were used; Polyacrylate polymer (CAD-Temp; CT), fiber-glass-reinforced polymer (Everest C-Temp; ET), and Polyetherether ketone (PEEK, BioHPP; PK) (Table 1). A sample size of ten specimens in each group was necessary to provide a 0.95 power using a 0.05 threshold of significance, according to the power analysis (size effect = 2.34, -two tailed=. 05) [12].

Table 1 Materials used in the study

Specimen preparation and grouping

For the experimental setup, thirty specimens (10 × 3 mm) of each type of provisional CAD/CAM material were produced using an ISOMET (Techcut4, Allied, USA). To ensure uniform specimen thickness, a digital caliper (Mitutoyo Corporation, Tokyo, Japan) was used. After finishing the bonded surfaces of the specimens using silicon carbide papers in grit levels ranging from 600 to 2000, distilled water was used for a 3-minute ultrasonic cleaning procedure. One side of the specimens was left exposed for surface treatment and bonding procedures, and then they were fixed in acrylic resin blocks (Paladur, Heraeus-Kulzer, Hanau, Germany) [3, 6].The experimental specimens were divided into one of the following three subgroups (n = 10) (Table 2) based on surface pretreatments: C; Surfaces of the specimens were not subjected to any surface treatment, SB; Surfaces were airborne particle abraded with 50 μm aluminum oxide (LEMAT NT4, Wassermann, Germany) for 10 s at a distance of 10 mm with a pressure of 0.55 MPa, and then air-dried for 20 s [14, 20, 21], and SB-T; Surfaces of the specimens were subjected to the same procedures as group SB with the addition of thermocycling before and after pretreatment. 5000 thermocycles (SD Mechatronic GmbH, Feldkirchen Westerham, Germany) at temperatures ranging from 5 to 55 °C for dwell times of 30 s and transfer times of 10 s were applied to group SB-T before and after repairing [14].

Table 2 Experimental groups in the study

Bonding procedure

According to the manufacturer’s recommendation, Visio. Link primer (Bredent GmbH & Co., Senden, Germany) was applied with a micro brush and then immediately polymerized for 20 s using a LED light (Elipar Freeligh 2, 3 M ESPE, 1,226 mW/cm²). Using a 6-mm diameter circular split Teflon mold, a nanohybrid repair resin composite (Filtek Supreme XTE) was packed onto treated CAD/CAM surfaces. To fill the mold, 2-mm thick resin composite layers were incrementally applied, and each layer was light-cured. Following that, the SB-T specimens were subjected to 5000 thermocycles between 5 and 55 °C for a dwell time of 30 s and a transfer time of 10 s [14].

Shear bond strength (SBS) test

The SBS test was carried out on a universal testing machine (AGS-1000 A; Shimadzu CO., Kyoto, Japan). The bonded CAD/CAM polymer-resin composite assembly was positioned in the machine’s lower jaw so that it was parallel to the direction of the shear force (Fig. 1). At a crosshead speed of 0.5 mm/min, a compressive loading was applied. The testing device’s upper moveable compartment was attached to a stainless-steel rod with a mono-beveled chisel configuration, and this rod was precisely positioned on the interface [3, 22, 23]. The testing machine displayed in Newton (N) the shear force at fracture (the force level at which the specimen debonds) using a 2.5 kN load cell connected to a computer. By dividing the fracture load (F) in Newton by the bonded surface area (A) in mm2, the SBS in megapascals (MPa) was computed. The bonded surface area was computed using a digital caliber (Mitutoyo Corporation, Tokyo, Japan). After debonding, the mode of failure was determined by examining the fractured specimen under a 20-x optical stereomicroscope (Olympus SZ61, Tokyo, Japan) and was divided into three categories: cohesive failure within the resin composite, adhesive type failure at the interface, and mixed type failure.

Fig. 1
figure 1

Shear Bond Strength Testing

Scanning electron microscopy evaluation

Three additional representative specimens from each material (10 mm × 10 mm × 1 mm) were prepared and cleaned with 96% ethanol in an ultrasonic bath for two minutes, then air-dried to assess the surface topography both before and after airborne particle abrasion. For the qualitative investigation of each material, specimens were mounted on metallic stubs, gold sputter-coated, and then examined under a SEM (Jeol-JSM-6510, Tokyo, Japan) with an initial magnification of 1000 x [3, 24].

Statistical analysis

The normality and equal variance assumptions were fulfilled according to the Shapiro–Wilk test and Levene’s test. Subsequently, statistical analyses (SPSS 22.0; IBM statistics) of the shear bond strength were analyzed using Two-way ANOVA to determine statistically significant differences and to detect the interaction between the two independent variables (material type and the surface conditioning). Tukey’s significant difference test was used for post-hoc comparisons. The level of significance was set at 5% for all statistical tests.

Results

The means and standard deviations of repair SBS values (MPa) for all groups are presented in Table 3. One-way ANOVA showed significant differences (p < .001) among the three-surface conditioning sub-groups for the three tested materials. Tukey’s multiple comparison tests showed that, the highest mean repair SBS values (17.84 MPa) were recorded for Everest C-temp in group SB, whereas the lowest repair SBS values (5.51 MPa) were recorded for CAD-temp in group C. SB group recorded significantly higher repair SBS values (p < .001) compared to other groups (C and SB-T) for CAD-temp and Everest C-temp. No significant differences (p\(>\)0.05) were detected between SB and SB-T groups for PEEK material. For CAD-temp, the highest mean repair SBS values were recorded for group SB (10.96), whereas the lowest repair SBS values were recorded for group C (5.551). For Everest C-temp, the highest mean repair SBS values were recorded for group SB (17.84), whereas the lowest repair SBS values were recorded for group SB-T (9.88). As for PEEK, the highest mean repair SBS values were recorded for group.

Table 3 Means (standard deviations) of Repair Bond Strength of Experimental Groups

SB-T (17.84), whereas the lowest repair SBS values were recorded for group C (8.67). Independent variables (Material type and surface conditioning) and their interactions were significantly affecting repair SBS values as shown by the two-way ANOVA table (Table 4).

Table 4 Two-way ANOVA table for repair shear bond strength (MPa)

The modes of failure frequencies in all groups and materials are presented in Table 5. Regarding the type of materials, the highest percentage of adhesive failures were observed in CAD-Temp, while the highest percentage of mixed and cohesive failures were observed in Everest C-Temp and PEEK, respectively. Regarding the surface treatment groups, adhesive failures were the most prominent type of failure (100%) in the control group at CAD-Temp. In the air-borne particle abrasion, mixed type of failure was the prominent type in Everest C-Temp (50%) and PEEK (60%). In the air-borne particle abrasion after thermocycling, adhesive failure was the predominant type in CAD-Temp (80%), while mixed types of failures occurred in Everest C-Temp (50%) and PEEK (70%).

Table 5 Failure pattern of the experimental groups

The surfaces of CAD-Temp, Everest C-temp, and PEEK under SEM showed variations in the surface microstructures (Fig. 2). CAD-Temp showed spherical areas of widely varying extensions that were obviously embedded in the resin matrix material (Fig. 2A). While Everest C-temp group showed irregular shaped long fibers intervening between them spherical shaped fillers particles with homogenous distribution within the materials (Fig. 2B). As for the PEEK group, it showed homogenous topography without voids or morphological defects (Fig. 2C).

Fig. 2
figure 2

SEM micrographs (1000- X) of CAD-Temp (A) Everest C-Temp (B) and PEEK (C)

Discussion

In this study, three different CAD/CAM materials for long-term provisional restoration were investigated. These materials need to be layered with a resin composite and are recommended by their manufacturers as framework materials for implant-supported fixed prostheses. Repair restorations are typically required after months or years of clinical service since they were thermally cycled extensively in intraoral conditions. Thermocycling might reduce the residual monomer content by reducing the number of carbon-carbon double bonds. Moreover, thermocycling might lead to mechanical stress on the bonding area of the repaired substrate. However, it is also suggested that thermocycling may improve repair bond strength by increasing the post-polymerization process between polymeric CAD/CAM materials and adhesive resins [14, 25]. Additionally, there is insufficient information available regarding their repairability.

Depending on the reason and extent of the restoration fracture, intraoral repair with resin composite may be a simple and less expensive alternative to extraoral repair. Repair of restorations requires the surface to be pretreated to enhance the adhesion of repair resin composite to restorations [12, 14]. A variety of factors influence the bond strength of the repaired restoration, including the substrate’s surface condition and its chemical microstructure. The shear bond strength test is a dependable and simple in vitro test method for determining the bond strengths of materials with a relatively large surface area (typically 3–6 mm in diameter) [18]. As a result, shear bond strength tests were performed in this study to assess the bond strength of repaired specimens [26, 27].

Thermocycling is an in vitro simulation of the moist oral environment to test the durability of bonding prior to clinical recommendation [19, 28]. Therefore, the ageing of restorations should be considered and included in the repair plan [28]. In this study, the specimens were aged through 5000 thermal cycles to obtain aged substrate surfaces. In addition, the experimental specimens were thermally aged again (5000 thermal cycles) after repair to mimic clinical conditions and evaluate the long-term durability of the bond by simulating six months of clinical.

use [29].

Numerous methods have been conducted to improve the surface properties of provisional materials, such as air abrasion, laser treatment, sulfuric acid etching, and so on. Although 98% sulfuric acid etching produced the highest bond strength with PEEK material, it is not clinically viable because of its corrosive activity. In this study, micromechanical retention can be provided through airborne particle abrasion. It has been reported that it is the easiest way to improve the microroughness and increase the surface area of polymer-based dental materials for sufficient bonding [30, 31]. As a result, the current study aimed to assess the effect of airborne-particle abrasion as a surface treatment and ageing on the repairability of three different CAD/CAM long-term provisional restoration polymers.

Based on the ANOVA test, the two independent variables (material type and surface treatment) revealed a statistically significant effect (p < .001) on the repair SBS values. Consequently, the first two null hypotheses were rejected.

The minimum acceptable SBS value at the interface between resin-based materials and the substrate is 5 MPa, according to the specifications of ISO 10,477 [32]. On the other hand, Beher et al. [33] suggested that the clinically acceptable SBS value is 10 MPa. This clinical requirement was met in all groups except the C and SB -T groups in CAD -Temp, the SB -T group in C-Temp, and the C group in PEEK. Bond strength levels can vary widely depending on study design; hence, it is advisable to proceed with caution when applying laboratory bond strength results to clinical criteria.

According to the results of the study, Everest C-Temp had significantly the highest repair SBS (17.84 ± 0.19) in the SB group among the three tested materials (Table 3). This could be attributed to the irregular surface topography, as shown in Fig. 2B, which could facilitate the penetration of the adhesive resin and thus improve the interlock between the substrate and the repair materials. Moreover, C-Temp has a higher glass fiber content and is a high performance continuous molecular plastic polymer chain suitable for both adhesive resin and repair material penetration. These results are consistent with the Wiegand et al. study [18], where it was suggested that the higher SBS with C-Temp may be due to the ability of the adhesive to penetrate glass fiber-related surface irregularities and improve retention. Regarding PEEK, it recorded significantly the second highest repair SBS because air particle abrasion altered the surface morphology of PEEK and facilitated adhesive resin penetration into the substrate, improving micromechanical interlock and potentially increasing bond strength [30, 31, 34].

Thermal cycling is widely utilized to mimic the frequently changing temperatures in the oral environment. These thermal changes may lead to a reduction in bond strength. In the present study, thermocycling considerably decreased the repair SBS of CAD-Temp. This could be explained by its high polymeric content (83–86 wt% PMMA), which is susceptible to water penetration between polymer chains’ gaps and separating them from one another, causing water absorption and ultimately leading to resin matrix softening that has a detrimental effect on SBS [3].Thermocycling, on the other hand, decreased SBS of C-Temp because wet environments cause a glass fiber’s surface to corrode as a result water penetrating through the polymer matrix, lowering mechanical properties and, as a result, bond strength [3, 35]. Additionally, thermocycling increased the SBS of PEEK since thermocycling may improve repair bond strength by increasing the post-polymerization process between polymeric CAD/CAM materials and adhesive resins [25].

The third null hypothesis was partially accepted because there was no statistically significant effect of thermocycling on SBS in PEEK material. Since they contain a highly cross-linked polymer with 20% ceramic filler (with a grain size of 0.3 to 0.5 m) that can penetrate and seal the space between the PEEK polymer’s chains, reducing chain mobility and minimizing water penetration, this may be explained by their low water sorption ability value. PEEK has a water sorption value of (≤ 6,5 µg/mm³), CAD-Temp has a value of (≤ 40 µg/mm³), and Everest C-Temp has a value of (9,6 µg/mm3) [36, 37]. Neim et al. [38] observed that PEEK is not significantly affected by thermocycling in their analysis of the effects of 5000 thermocycling cycles on the physicomechanical properties of numerous CAD/CAM restorative materials. Additionally, Libermann et al. [15] evaluated how different ageing processes affected the water sorption of several CAD/CAM polymers. They came to the conclusion that storage media had no statistically significant impact on PEEK’s ability to absorb water.

Any change in the surface features of the tested material may affect the SBS values [7, 21]. In this study, a high percentage of adhesive failures occurred at CAD-Temp due to the insufficient bond strength of the repair resin on CAD-Temp [7, 19]. Furthermore, Everest C-Temp and PEEK were found to have a higher incidence of mixed failures, owing to uneven shear force distribution at the resin-restoration interface. The results are supported by a shift from adhesive to mixed failure when bond strength was increased. Clinical relevance for successful bonding on CAD/CAM surfaces can be achieved by surface roughening and the selection of a suitable adhesive system.

The present study has some limitations; Only one type of repair veneering resin and one adhesive system were used, so the results of this study cannot be generalized to other commercially available repair systems. In addition, different surface treatments such as etching solutions and the use of different adhesive systems, need to be further investigated. Furthermore, long-term clinical performance should also be evaluated in a clinical study with a controlled, standardized study design.

Conclusions

Within the limitations of this in vitro study, it is concluded that the three tested CAD/CAM polymers can be adequately repaired after airborne-particle abrasion surface pretreatment. Everest C-temp recorded the highest repair SBS after airborne particle abrasion. Although, repair SBS was significantly reduced by thermocycling in both CAD-Temp and Everest C-Temp, PEEK was not significantly affected. PEEK and Everest C-Temp can be recommended for clinical use as long term, durable provisional materials.

Data Availability

This article has all the data that were collected or analyzed during this study.

References

  1. Stawarczyk B, Ender A, Trottmann A, Özcan M, Fischer J, Hämmerle CHF. Load-bearing capacity of CAD/CAM milled polymeric three-unit fixed dental prostheses: effect of aging regimens. Clin Oral Invest. 2012;16:1669–77.

    Article  Google Scholar 

  2. Alt V, Hannig M, Wöstmann B, Balkenhol M. Fracture strength of temporary fixed partial dentures: CAD/CAM versus directly fabricated restorations. Dent Mater. 2011;27:339–47.

    Article  PubMed  Google Scholar 

  3. Soliman TA, Ghorab S, Baeshen H. Effect of surface treatments and flashfree adhesive on the shear bond strength of ceramic orthodontic brackets to CAD/CAM provisional materials. Clin Oral Invest 2022 Jan;26(1):481–92.

  4. Rayyan MM, Aboushelib M, Sayed NM, Ibrahim A, Jimbo R. Comparison of interim restorations fabricated by CAD/CAM with those fabricated manually. J Prosthet Dent. 2015;114:414–9.

    Article  PubMed  Google Scholar 

  5. Lodding DW. Long-term esthetic provisional restorations in dentistry. Curr Opin Cosmetic Dent. 1997;4:16–21.

    Google Scholar 

  6. ELSyad MA, Soliman TA, Khalifa AK. Retention and Stability of rigid telescopic and Milled Bar Attachments for Implant-Supported Maxillary Overdentures: an in Vitro Study. Int J Oral Maxillofac Implants. 2018;33(5):e127–33.

    Article  PubMed  Google Scholar 

  7. Astudillo-Rubio D, Delgado-Gaete A, Bellot-Arcís C, Montiel- Company JM, Pascual-Moscardó A, Almerich-Silla JM. Mechanical properties of provisional dental materials: a systematic review and meta-analysis. PLoS ONE. 2018;13:e0193162.

    Article  PubMed  PubMed Central  Google Scholar 

  8. Abdulmohsen B, Parker S, Braden M, Patel MP. A study to investigate and compare the physicomechanical properties of experimental and commercial temporary crown and bridge materials. Dent Mater. 2016;32:200–10.

    Article  PubMed  Google Scholar 

  9. Alp G, Murat S, Yilmaz B. Comparison of flexural strength of different CAD/CAM PMMA-based polymers. J Prosthodont. 2019;28:e491–5.

    Article  PubMed  Google Scholar 

  10. Chavali R, Nejat AH, Lawson NC. Machinability of CAD-CAM materials. J Prosthet Dent. 2017 Aug;118(2):194–9.

  11. Şişmanoğlu S, Gürcan AT, Yıldırım-Bilmez Z, Turunç-Oğuzman R, Gümüştaş B. Effect of surface treatments and universal adhesive application on the microshear bond strength of CAD/CAM materials. J Adv Prosthodont. 2020 Feb;12(1):22–32.

  12. Sismanoglu S, Yildirim-Bilmez Z, Erten-Taysi A, Ercal P. Influence of different surface treatments and universal adhesives on the repair of CAD-CAM composite resins: An in vitro study. J Prosthet Dent. 2020 Aug;124(2): 238.e1-238.e9.

  13. Reeponmaha T, Angwaravong O, Angwarawong T. Comparison of fracture strength after thermo-mechanical aging between provisional crowns made with CAD/CAM and conventional method J Adv Prosthodont. 2020 Aug;12(4):218–24.

  14. Wiegand A, Stucki L, Hoffmann R, Attin T, Stawarczyk B. Repairability of CAD/CAM high-density PMMA- and composite-based polymers. Clin Oral Investig. 2015 Nov;19(8):2007–13.

  15. Liebermann A, Wimmer T, Schmidlin PR, Scherer H, Löffler P, Roos M, Stawarczyk B. Physicomechanical characterization of polyetheretherketone and current esthetic dental CAD/CAM polymers after aging in different storage media. J Prosthet Dent. 2016;115(3):321–8e2.

    Article  PubMed  Google Scholar 

  16. Barto A, Vandewalle KS, Lien W, Whang K. Repair of resin-veneered polyetheretherketone after veneer fracture. J Prosthet Dent. 2021;125(4): 704.e1-704.e8.

  17. Mjör IA, Gordan VV. Failure, repair, refurbishing and longevity of restorations. Oper Dent. 2002;27(5):528–34.

    PubMed  Google Scholar 

  18. Brendeke J, Ozcan M. Effect of physicochemical aging conditions on the composite-composite repair bond strength. J Adhes Dent. 2007;9(4):399–406.

    PubMed  Google Scholar 

  19. Tezvergil A, Lassila LV, Vallittu PK. Composite-composite repair bond strength: effect of different adhesion primers. J Dent. 2003;31(8):521–5. https://doi.org/10.1016/S0300-5712(03)00093-9.

    Article  PubMed  Google Scholar 

  20. Caglar I, Ates SM, Duymus ZY. An in vitro evaluation of the effect of various adhesives and surface treatments on bond strength of resin cement to pol-yetheretherketone. J Prosthodont. 2018;28:342–9.

    Article  Google Scholar 

  21. Ates SM, Caglar I, Duymus ZY. The effect of different surface pretreatments on the bond strength of veneering resin to polyetheretherketone. J Adhes SciTechnol. 2018;32:1–12.

    Google Scholar 

  22. Klocke A, Kahl-Nieke B. Influence of force location in orthodontic shear bond strength testing. Dent Mater. 2005;21:391–6. https://doi.org/10.1016/j.dental.2004.07.004.

    Article  PubMed  Google Scholar 

  23. -Dental materials - testing of adhesion to tooth structure. Second ed. Switzerland: 2003. Technical specification ISO/TS 11405.

  24. Al-Gerny YA, Ghorab SM, Soliman TA. Bond strength and elemental analysis of oxidized dentin bonded to resin modified glass ionomer based restorative material. J Clin Exp Dent. 2019;11(1):e250–6.

    PubMed  PubMed Central  Google Scholar 

  25. Naga AE, Zahran A. The Microshear Bond Strength of Repaired Resin Composite after different surface and bonding treatments. J Am Sci. 2017;13:79–86.

    Google Scholar 

  26. Flury S, Peutzfeldt A, Lussi A. Influence of increment thickness on microhardness and dentin bond strength of bulk fill resin composites. Dent Mater. 2014;30:1104–12.

    Article  PubMed  Google Scholar 

  27. Hickel R, Br€ushaver K, Ilie N. Repair of restorations–criteria for decision making and clinical recommendations. Dent Mater. 2013;29:28–50.

    Article  PubMed  Google Scholar 

  28. Çelik EU, Ergücü Z, Türkün LS, Ercan UK. Tensile bond strength of an aged resin composite repaired with different protocols. J Adhes Dent. 2011;13:359–66.

    PubMed  Google Scholar 

  29. Soliman TA, Raffat EM, Farahat DS. Evaluation of mechanical behavior of CAD/CAM polymers for long-term interim restoration following Artificial Aging. Eur J Prosthodont Restor Dent. 2022 Apr;19. https://doi.org/10.1922/EJPRD_2392Soliman09.

  30. Zhou L, Qian Y, Zhu Y, et al. The effect of different surface treatments on the bond strength of PEEK composite materials. Dent Mater. 2014;30:209–15.

    Article  Google Scholar 

  31. Schmidlin PR, Stawarczyk B, Wieland M. Effect of different surface pre-treatments and luting materials on shear bond strength to PEEK. Dent Mater. 2010;26:553–9.

    Article  PubMed  Google Scholar 

  32. ISO. (2020) ISO 10477 Dentistry-polymer-based crown and veneering materials. Geneva: International Organization for Standardization. Available at: https://www.iso.org/standard/80007.html.

  33. Behr M, Rosentritt M, Gröger G, Handel G. Adhesive bond of veneering composites on various metal surfaces using silicoating, titanium-coating or functional monomers. J Dent. 2003;31:33–42.

    Article  PubMed  Google Scholar 

  34. Stawarczyk B, Basler T, Ender A. Effect of surface conditioning with airborne-particle abrasion on the tensile strength of polymeric CAD/CAM crowns luted with self-adhesive and conventional resin cements. J Prosthet Dent. 2012;107:94–101.

    Article  PubMed  Google Scholar 

  35. Khan AS, Azam MT, Khan M, Mian SA, Ur Rehman. I. An update on glass fiber dental restorative composites: a systematic review. Mater Sci Eng C Mater Biol Appl. 2015;47:26–39.

    Article  PubMed  Google Scholar 

  36. Everest C, Temp. provisional restoration (2016) KaVo Elements for KaVo ARCTICA and KaVo Everest. The foundation for reliable long-term temporary applications: C-Temp. IOP Publishing Physics Web. http://dinamed.by/media/Instrukcii2014/ARCTICA_en_Material.pdf. Accessed 29 August 2020.

  37. PEEK BIOHPP, Bredent UK. The new class of materials in prosthetics. https://www.bredent.co.uk/wpcontent/uploads/2017/02/BioHPP-2013.pdf. Accessed 10 july 2021.

  38. Niem T, Youssef N, Wöstmann B. Influence of accelerated ageing on the physical properties of CAD/CAM restorative materials. Clin Oral Investig. 2020;24:2415–25.

    Article  PubMed  Google Scholar 

Download references

Acknowledgements

Not applicable.

Funding

No funding was received.

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Author information

Authors and Affiliations

Authors

Contributions

Conceptualization: TS, AR and YG; Experimental work: TS, EH; Interpretation of data: AR, YG, EH; writing original draft:EH prepared Fig. 1: TS; review and editing: TS. All authors have read and agreed to the published version of the manuscript.

Corresponding author

Correspondence to Tarek Ahmed Soliman.

Ethics declarations

Ethics approval and consent to participate

Not applicable.

Consent for publication

Not applicable.

Competing interests

The authors affirm that they have no competing interests with regard to this study. The companies mentioned in this study are not associated with the authors or provide them with advantages.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Soliman, T.A., Robaian, A., Al-Gerny, Y. et al. Influence of surface treatment on repair bond strength of CAD/CAM long-term provisional restorative materials: an in vitro study. BMC Oral Health 23, 342 (2023). https://doi.org/10.1186/s12903-023-03021-y

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s12903-023-03021-y

Keywords