The effect of nanobased irrigants on the root canal dentin microhardness: an ex-vivo study

BMC Oral Health volume 23, Article number: 581 (2023) Cite this article

Abstract

Background

Given the favorable antimicrobial properties of zinc oxide (ZnONPs), standard silver (AgNPs), and imidazolium-based silver (Im-AgNPs) nanoparticles, this study aimed to evaluate their influence on the microhardness of root canal dentin.

Methods

In this experimental study, 40 mandibular premolars were decoronated at the cementoenamel junction and longitudinally sectioned into halves to create 80 specimens. They were randomly allocated to 5 groups (n = 16) and irrigated with ZnONPs, AgNPs, Im-AgNPs, NaOCl, or normal saline (as the negative control) for 15 min. The Vickers Hardness Number (VHN) was measured on each root canal third before and after being soaked in irrigants. Statistical analysis was performed using paired t-test, one-way ANOVA, and post hoc Tukey’s test (α = 0.05).

Results

Im-AgNPs and ZnONPs irrigants improved the microhardness of root dentin, whereas, AgNPs and NaOCl decreased it. ZnONPs yielded the highest VHN at the coronal third (P˂0.001), while the Im-AgNPs provided the highest VHN at the middle and apical thirds (P˂0.001). The AgNPs group showed the lowest VHN at the apical third.

Conclusions

The irrigants containing Im-AgNPs and ZnONPs significantly enhanced the root dentin microhardness. However, the use of AgNPs resulted in decreased microhardness.

Peer Review reports

Background

The foremost aim of root canal treatment is to eradicate microorganisms and their by-products from the root canal system [1, 2]. Although various irrigants have been recommended over the years to enhance root canal disinfection and endodontic treatment success [3, 4], no single solution has yet met all the criteria of an ideal endodontic irrigant. Currently, sodium hypochlorite (NaOCl) is considered the gold standard due to its high efficacy AgNPs against bacteria and biofilm, as well as its ability to dissolve organic debris [5,6,7]. However, it has several drawbacks including an unpleasant taste, toxicity, incomplete elimination of the smear layer, and negative effects on dentin flexural strength [3, 8]. Consequently, researchers continue to seek alternative irrigants with greater efficacy and fewer side effects [5].

Nanotechnology, a brilliant achievement of the last decade, has revolutionized science research and development [9, 10]. Some nanoparticles, such as silver (AgNPs), possess remarkable antimicrobial properties [11, 12], even AgNPs against drug-resistant pathogens such as E. faecalis [13, 14], which is due in part to their nano size, which enables them to penetrate microorganisms’ cell membrane more effectively. Imidazolium-coated silver (Im-AgNPs) nanoparticles, engineered specifically for endodontic applications, have gained popularity as potential root canal irrigants due to their antimicrobial properties, biocompatibility, and other promising features [15,16,17]. Abbaszadegan et al. [18] found that positively-charged Im-AgNPs nanoparticles had a significant impact on the antibacterial activity of this novel irrigant AgNPs against E. faecalis. Moreover, these nanoparticles resulted in higher surface roughness and were biocompatible and cytocompatible with L929 cells, while exhibiting low cytotoxicity compared to commonly used irrigants such as sodium hypochlorite and chlorhexidine [18,19,20,21].

Zinc oxide (ZnONPs) is another metal nanoparticle with promising antibacterial activity even against antimicrobial resistant microorganisms [22] and favorable properties for use in Endodontics, as it exhibits selective toxicity against dental bacterial pathogens with minimal effect on human cells [23, 24]. In addition, ZnONPs nanoparticles have been reported to improve the physical and chemical features of the Grossman sealer [25]. Some nanobased irrigants (e.g. AgNPs, ZnONPs, and titanium dioxide) have been found to enhance the fracture resistance of endodontically treated teeth [26].

Some root canal irrigants, such as NaOCl and ethylenediaminetetraacetic acid (EDTA), can affect the structural characteristics of dentin like microhardness, and consequently impact the quality of obturation and coronal restoration [27,28,29]. Given the absence of a similar study, the current study aimed to assess the microhardness of root canal dentin after treatment with standard AgNPs, Im-AgNPs, and ZnONPs nanoparticles compared with 2.5% NaOCl and normal saline. The null hypothesis was that these irrigants would not significantly affect the dentin microhardness.

Methods

Sample size calculation

Following previous research [30], a power calculation was conducted by using the chi-square test family and variance statistical test (G*Power 3.1 software; Heinrich Hein University, Dusseldorf, Germany) with a significance level of α = 0.05 and a power of ß=0.95. The minimum sample size was determined to be 12 per group.

Preparation of tooth samples

This ex-vivo experimental study was ethically approved by the Ethics Committee of Shiraz University of Medical Sciences (IR.SUMS.DENTAL.REC.1400.043). It was performed in full accordance with ethical principles, including the World Medical Association Declaration of Helsinki (version 2008). The study design for the present experiment was based on the methodology of Saha et al. [31]. Forty mandibular premolars extracted for orthodontic purposes were collected with written informed consent from patients. The teeth were cleaned of any soft tissue or calculus deposits and stored in 0.1% thymol solution under refrigeration until used. Proximal view radiographs were taken to confirm the presence of a single patent canal. Teeth with root caries, cracks, curved canals, a history of endodontic treatment, internal resorption, or calcification were excluded. The specimens were decoronated at the cementoenamel junction using a double-faced diamond disc (Microdont, LDA, Brazil) at low speed under water cooling to ensure a uniform sample length of 15 ± 1 mm root length.

Specimen preparation

Plastic cubes (with dimensions of 3 × 3 × 3 cm3) were filled with transparent polyester material, and the extracted teeth were inserted with the dentinal surface fronting outward. The resulting blocks were then longitudinally sectioned under water cooling, resulting in 80 dentin halves. These sections were examined at 4× magnification using a Dino-Lit USB Digital Microscope (AM3111-0.3 MP; Dino-Lit, Vietnam) to identify and exclude any cracked teeth. Surface scratches were then ground-polished under water coolant using a series of ascending grades of carbide abrasive papers (500, 800, 1000, and 1200 grit) (Bigo, Dent Product, Germany), followed by a final polish with a 0.1-mm alumina suspension on a rotary felt disc (Microdont, LDA, Brazil) to achieve a smooth glossy mirror-like surface.

The specimens were randomly (simple randomization) allocated to 5 groups (n = 16 per group) to receive irrigation with any of standard AgNPs, Im-AgNPs, 0.1% ZnONPs (Nano-Mavad-Gostaran Pars, Tehran, Iran), 2.5% NaOCl (Sigma-Aldrich Corporation, St Louis, MO, USA), or normal saline (as the negative control).

Synthesis of standard AgNPs nanoparticles

Silver nitrate powder was purchased from Merck, Darmstadt, Germany. The synthesis protocol was as follows; 50 mL of 1 mM silver nitrate (AgNO3) solution was mixed with 1.0 mL of 1 mM trisodium citrate in a 100-mL volumetric flask and stirred vigorously. After 15 min, 50 µL of 100 mM sodium borohydride solution was rapidly added to this mixture solution. The color of the solution initially turned pale yellow and later turquoise. When the solution cooled to room temperature, it was centrifuged at 5000 rpm for 10 min. The supernatant was discarded and the pellet was air-dried in an incubator [15, 32,33,34,35].

Synthesis of Im-AgNPs irrigant

Twenty mL of 1-dodecyl-3-methylimidazolium chloride (6.2 mM) (Sigma-Aldrich corporation, St Louis, MO, USA) was mixed with an aqueous solution of AgNPsNO3 (0.01 M) and vigorously stirred. An aqueous solution of 0.4 M NaBH4 was instantly added dropwise to the mixture overnight to obtain a golden-colored solution. The colloidal solution was centrifuged for 20 min to eliminate unreacted ions. The initial concentration of the nanoparticle solution before the experiment was 1024 µg/mL.

Synthesis of ZnONPs

To synthesize the ZnONPs solution, the ZnONPs powder (Nano-Mavad-Gostaran Pars, Tehran, Iran) was dissolved in phosphate-buffered saline solution and stirred on a magnetic stirrer for 24 h. The solution was then sonicated to ensure homogeneity.

Characterization of nanoparticles

The nanoparticles were subjected to multiple characterization techniques, including ultraviolet-visible spectroscopy (UV-2550, Shimadzu, Japan), transmission electron microscopy ([TEM], Zeiss-EM10C-100 KV, Germany), X-ray diffraction spectroscopy ([XRD], Siemens D5000 diffractometer, Karlsruhe, Germany), field emission scanning electron microscope (FESEM, Sigma VP, ZEISS, Germany, Energy-dispersive X-ray spectroscopy ([EDS], FESEM, Sigma VP, ZEISS, Germany), and Zeta potential measurements (Zeta-DLS; Zetasizer, Malvern, England). The Im-AgNPs were lyophilized in the same way as the dried standard silver nanoparticles for above mentioned characterization studies.

Measurement of dentin microhardness

To measure the pre-treatment microhardness, each sample was individually mounted on the stage of the Vickers microhardness testing machine (FM 700, Future-T,ech, Tokyo, Japan) and three indentations were marked at each root canal third (middle, apical, and coronal) by using a Vickers diamond indenter at a 300 gr load and a 20-second dwell time [31]. To standardize the measurements, indentations were made on the dentin surface at approximately 200 μm from the dentin-canal interface. The Vickers hardness value was calculated by dividing the applied load by the area of the sloping faces of the indentations. The resulting impression of the two diagonals was observed through an optical microscope, the average length of the two diagonals was measured by the built-in scaled micrometer and converted into the Vickers hardness number (VHN) using the following formula:

VHN (HV) = 1.854(F/D2)

The formula’s constant value was calculated based on the specific geometry of the indenter, where F represents the applied load (grams) and D represents the diagonal of the indentation (µm) [36].

For the pre-treatment VHN, three indentations were marked on each root canal third (middle, apical, and coronal), and the average VHNs was calculated for each third. The specimens were randomly allocated into 5 groups (n = 16) and immersed in 5 mL of standard AgNPs, Im-AgNPs, ZnONPs, and NaOCl nanobased irrigants, as well as normal saline as the negative control, for 15 min. Following immersion, the specimens were rinsed with normal saline, and dried, and the post-treatment VHN was measured using the same method as for the pre-treatment VHN.

Statistical analysis

The data were statistically analyzed by using SPSS software (version 16, SPSS INC., Chicago, IL, USA) through one-way ANOVA (for intergroup comparison), Tukey’s post hoc test (for pairwise comparison of the groups regarding the mean hardness), and paired t-test (to compare the effect of irrigants). P values ˂0.05 were considered significant.

Results

Synthesis and characterization of nanobased irrigants

Ultraviolet-visible spectroscopy

Figure 1 shows the UV-visible spectra of AgNPs, Im-AgNPs, and ZnONPs irrigants. The spectrum of AgNPs and Im-AgNPs exhibited characteristic peaks at around 440 nm and 428 nm, respectively, confirming the formation of AgNPs nanoparticles resulting from the reduction of AgNPs+ ions to AgNPs0. Previous findings indicated that the absorption bands at around 400 nm in the UV-visible spectrum are attributed to the spherical AgNPs nanoparticles [37]. The ZnONPs group showed a characteristic peak at a wavelength of 376 nm, indicating the formation of ZnONPs nanoparticles from zinc nitrate solution. This was further supported by the observed color alteration from dark brown to light brown due to the synthesis of ZnONPs nanoparticles. This wavelength is consistent with the reported characteristic peak of ZnONPs in the literature [38, 39].

Fig. 1
figure 1

The UV-visible spectrum of AgNPs, Im-AgNPs, and ZnONPs irrigants

Full size image

Energy-dispersive X-ray spectroscopy

The EDS analysis results of the nanoparticles showed different elemental compositions for each group. The AgNPs nanoparticles had carbon (43.4%), oxygen (28.8%), and AgNPs (27.8%) elements. The Im-AgNPs had a strong AgNPs signal (56.9%), as well as carbon (29%), oxygen (7.1%), and nitrogen (7%) elements. The EDS analysis of ZnONPs nanoparticles demonstrated the presence of oxygen (22%) and zinc elements (78%), confirming the formation of zinc oxide (Fig. 2).

Fig. 2
figure 2

The EDS analysis of synthesized nanoparticles; (a) AgNPs (b) Im-AgNPs (c) ZnONPs

Full size image

Zeta potential

Based on the analysis of Zeta potential, the surface charge was + 16.47 in AgNPs, + 50.90 in Im-AgNPs, and − 7.44 in ZnONPs.

X-ray diffraction analysis

The XRD patterns of AgNPs and Im-AgNPs nanoparticles validated their crystalline nature, with diffraction peaks at 2θ = 39.113°, 43.488°, and 65.59° (Fig. 3), which were consistent with previous studies [37, 40,41,42]. Similarly, the XRD pattern of ZnONPs nanoparticles confirmed their crystalline nature, with peaks (and Miller indices) at 2θ = 32.2° (100), 34.4° (002), 36.3° (101), 46.2° (012), 56.7° (110), 63° (013), and 67.9° (112) (Fig. 4), which was in agreement with Lodhi et al.‘s study [43]. The absence of any additional peaks in the XRD pattern indicated the high purity of the product.

Fig. 3
figure 3

The XRD patterns of AgNPs and Im-AgNPs

Full size image
Fig. 4
figure 4

The XRD patterns of ZnONPs

Full size image

Transmission electron microscopy

The TEM images showed that the synthesized AgNPs, Im-AgNPs, and ZnONPs nanoparticles were all spherical in shape, confirming the results obtained from UV-visible spectroscopy (Fig. 5). The average size of 50 isolated particles from each TEM image was measured to calculate their mean sizes, which were 24.83 ± 11.96 nm in AgNPs, 27.17 ± 15.62 nm in Im-AgNPs, and 18.83 ± 6.25 nm in ZnONPs nanoparticles. The FESEM graphs of the synthesized NPs are demonstrated in Fig. 5. The average size of AgNPs, Im-AgNPs, and ZnONPs was calculated 10.74 nm, 11.17 nm, and 15.12 nm from FESEM micrographs.

Fig. 5
figure 5

The FESEM micrographs of the synthesized nanoparticles: A1) AgNPs B1) Im-AgNPs C1) ZnONPs/ The TEM images of the synthesized nanoparticles: A2) AgNPs B2) Im-AgNPs C2) ZnONPs

Full size image

Microhardness assessment

The Kolmogorov-Smirnov test showed that the data were normally distributed (P˃0.05). One-way ANOVA and post hoc Tukey’s test demonstrated that the pre-treatment VHNs were not significantly different among the groups (P˃0.05). The pre- and post-treatment VHNs were not significantly different in the control group (P˃0.05). Regardless of the root canal thirds, the VHN was the highest in the ZnONPs group, followed by Im-AgNPs, normal saline, NaOCl, and standard AgNPs groups, respectively (Table 1).

Table 1 Mean ± SD of root canal dentin microhardness following irrigation by experimental irrigants regardless of root canal thirds
Full size table

Immersion in standard AgNPs nanobased irrigant significantly decreased the VHN compared to normal saline in the apical and coronal thirds (P˂0.001). Conversely, immersion in Im-AgNPs significantly increased the VHN in the middle and apical thirds (P˂0.05). Immersion in standard AgNPs nanobased irrigant and NaOCl reduced the VHNs in the coronal and apical root canal thirds, with statistical significance observed in the coronal third of the root canal (P˂0.001). In the middle third, no significant difference was observed following immersion in standard AgNPs and NaOCl (P˂0.05). On the other hand, ZnONPs nanobased irrigant increased the VHN, particularly in the coronal third (P˂0.001). Pairwise comparison of post-treatment VHNs in different root canal thirds showed that the highest VHNs at the coronal and middle thirds were in the ZnONPs group (P˂0.001); while the highest VHN in the apical thirds was in the Im-AgNPs group (P˂0.001) (Table 2).

Table 2 Comparison of the pre- and post-treatment VHNs in each root canal third (paired t-test)
Full size table

Discussion

The UV-visible spectrum of AgNPs and Im-AgNPs showed characteristic peaks around 440 nm and 428 nm, respectively, which confirms the formation of AgNPs through the reduction of AgNPs+ ions to AgNPs0. According to earlier research, the spherical AgNPs nanoparticles contribute to absorption bands at around 400 nm in the UV-visible spectrum [37]. The 376-nm wavelength seen in the UN-visible spectrum is a characteristic peak of the ZnONPs group. This peak indicates the formation of ZnONPs nanoparticles from the zinc nitrate solution used in the synthesis, which was also confirmed by the visible color change from dark brown to light brown. The reported wavelength is consistent with previous literature on the characteristic peak of ZnONPs [38, 39].

The XRD analysis confirmed the crystalline nature of AgNPs and Im-AgNPs, as evidenced by the diffraction peaks at 2θ = 39.113°, 43.488°, and 65.59°; which were consistent with previous studies [37, 40,41,42]. The XRD pattern for ZnONPs showed characteristic peaks (and Miller indices) at various 2θ angles including 32.2° (100), 34.4° (002), 36.3° (101), 46.2° (012), 56.7° (110), 63° (013), and 67.9° (112) (Fig. 4), which were in agreement with Lodhi et al.‘s findings [43]. The absence of any extra peaks in this XRD pattern indicated the high purity of the product.

The null hypothesis was partially rejected as some nanobased irrigants significantly affected the microhardness of root canal dentin. The findings revealed that the application of AgNPs as root canal irrigant negatively influenced root dentin microhardness. Moreover, VHNs following the usage of Im-AgNPs significantly increased at the middle and apical third, while its raise at the coronal third was not significant. Besides, irrigation of the samples with AgNPs at the coronal third remarkably decreased the microhardness values. Final flushing of the root canals with ZnONPs solution improved the values of microhardness at all root canal thirds, but only at the coronal third its improvement was statistically significant. Sodium hypochlorite significantly reduced VHN at the coronal third.

The success of endodontic treatment depends on the quality and method of chemomechanical preparation, disinfection, and 3-dimensional obturation of the root canals [44,45,46]. Endodontic irrigants can alter the chemical composition of dentin by affecting its organic and inorganic phases, which can lead to a reduction in dentin microhardness and an increase in the risk of tooth fracture. Hence, irrigants should be cautiously chosen to maximize efficiency and minimize adverse impacts on root canal dentin [47].

In the evaluation of the physical properties of root dentin different parameters should be considered including roughness, hardness, and fracture resistance [16, 28, 48]. Hardness refers to the ability of a solid material to withstand plastic deformation, elastic deformation, and destruction. Teeth hardness is classified into static and dynamic. The most commonly utilized technique for characterization is static indentation hardness which includes Knoop hardness, Vickers hardness, and nano-hardness [49].

The effects and penetration depth of therapeutic materials used on dentin during root canal preparation depend on the diameter and number of dentinal tubules [50]. Moreover, the tubular density is inversely related to microhardness, as it increases towards the pulp chamber [51]. Therefore, in the present study, dentin microhardness was measured in different root canal thirds of radicular dentin. The dentin microhardness is also affected by the extent of mineralization and the presence of hydroxyapatite in the intertubular substance [31].

The current findings revealed that the baseline microhardness was higher in the coronal third compared to the middle and apical thirds. The mechanical behavior is significantly attributed to the mineral content [52]. The more condensed mineral content in the coronal third may be responsible for the greater baseline microhardness. This higher mineral content makes dentin more resilient and capable of resisting local deformation. This study showed that normal saline did not significantly affect the VHNs, which is consistent with previous studies that used normal saline as a negative control [29, 47, 53].

Organic materials (chiefly collagen type I) play an important mechanical role in dentin, accounting for 22% of its composition. NaOCl triggers the depletion of the organic phase, which can lead to mechanical alterations [54]. The present findings indicate that immersion in NaOCl caused a decrease in dentin microhardness compared to the pre-treatment values, with a statistically significant effect in the coronal zone of the root canal dentin. This may be due to the breakdown of long peptide chains and chlorination protein terminal groups by NaOCl, leading to the formation of other species [55].

Previous studies have extensively investigated the effect of NaOCl on dentin microhardness [27,28,29, 31, 36, 50, 55, 56]. Consistent with the present study, some studies have reported a significant decrease in dentin microhardness after exposure to 2.5% NaOCl [27, 36, 55]. Bosaid et al. [56] detected that a 5-minute application of 1.5% NaOCl decreased the dentin microhardness, although it was statistically insignificant. In contrast, Philip et al. [55] detected that 2.5% NaOCl significantly decreased dentin microhardness in the apical third compared to the middle and cervical thirds. This reduction was justified by the low surface tension of NaOCl, which allowed it to penetrate long and narrow dentinal tubules through capillary forces or by diffusion into the dentin.

In the current study, the primary concentration of NPs solution before the experiment was set as 1024 µg/mL since we intended to investigate whether different NPs in their highest effective antimicrobial concentration would affect other characteristics of a good irrigant, such as microhardness. Silver nanoparticles are known as a popular root canal irrigant because of their antibacterial properties and low toxicity on human cells [17, 34, 57, 58]. However, the present study found that using them as a root canal irrigant reduced the root dentin microhardness at all thirds of the root canal. In agreement with the current study, Suzuki et al. [59] reported that AgNPs nanoparticles caused little to no alterations in the mechanical properties of dentin and resin cement at different root canal thirds. On the contrary, Hassan et al. [60] observed that using AgNPs nanoparticles as an intracanal medicament gradually increased the microhardness of root canal dentin.

Baras et al. [61] assessed an innovative root canal sealer incorporating dimethylaminohexadecyl methacrylate (DMAHDM), AgNPs nanoparticles, and amorphous calcium phosphate nanoparticles, and detected that this sealer did not jeopardize the physical structure of root dentin such as hardness. On the other hand, Jowkar et al. [26] demonstrated that using AgNPs nanoparticles as the final irrigant improved the fracture resistance of teeth with previous endodontic treatment.

The present study and some previous ones [16, 62] showed that positively-charged AgNPs nanoparticles can enhance the mechanical properties of dentin. However, standard AgNPs nanoparticles used in this study exhibited opposing effects compared to the positively-charged variety (Im-AgNPs nanoparticles), indicating that the synthesis method can impact nanoparticles properties [63]. Possibly, the decrease in microhardness following irrigation with AgNPs irrigant is due to their generally negative surface charge, which can interfere with material properties.

To date, no previous research has investigated the impact of Im-AgNPs nanobased irrigant on root dentin microhardness. Im-AgNPs nanoparticles have demonstrated superior antibacterial activity, even at lower concentrations, when compared to chlorhexidine and NaOCl [15]. Farshad et al. [16] reported that Im-AgNPs nanoparticles modified the physicochemical properties of dentin and enhanced the roughness of root dentin. The underlying reasons were either due to the ionic liquid (imidazole) nature or the discrepancy in charge distribution on the cationic part of the imidazole and dentin surface.

As the first investigation into the effect of ZnONPs nanoparticles on dentin microhardness, the current findings demonstrated that this irrigant significantly elevated the dentin microhardness at the coronal third of the root canal. Conversely, Im-AgNPs nanoparticles significantly increased the microhardness at the middle and apical parts of the root. This improvement in microhardness following the use of Im-AgNPs nanoparticles may be attributed to the nature of the ionic liquid (imidazole) or uneven charge distribution on the cationic part of the imidazole and dentin surface. Zhu et al. [64] reported that the incorporation of AgNPs and zinc nanoparticles with mesoporous calcium-silicate nanoparticles did not have any detrimental effects on the mechanical characteristics of dentin. The absence of hydroxyl ions in the aqueous solutions of these nanoparticles was mentioned as the probable cause of negative alterations in dentin’s mechanical properties.

In line with the present findings, Jowkar et al. [26] observed that ZnONPs nanoparticles enhanced root fracture resistance in endodontically-treated teeth. Although they found no significant difference between the ZnONPs and AgNPs, they reported that AgNPs nanoparticles had a greater positive effect on root fracture resistance compared to ZnONPs. Another research addressed the influence of incorporating AgNPs and ZnONPs nanoparticles into pit and fissure sealant on the microhardness of these sealants. The results showed that the microhardness of sealants containing AgNPs increased more significantly compared to those containing ZnONPs nanoparticles. The researchers suggested that the higher increase in microhardness could be attributed to the nature of the nanoparticles, with metals being harder than metal oxides even at lower concentrations [65]. Possibly the contrasts between our findings and those of previous studies were due to variations in the synthesis methods or concentrations of nanoparticles used.

The present study highlights the potential of Im-AgNPs and ZnONPs nanoparticles as alternative root canal irrigants, as they not only possess antibacterial properties, but also improve dentin microhardness. However, more in-vivo and in-vitro studies are required to fully evaluate the efficacy of these novel nanobased irrigants, including their effect on other dentin properties such as roughness and fracture resistance, and at different distances from the pulp–dentine interface.

One major limitation of ex-vivo studies like this is the potential variation in teeth studied, including age differences, which could affect the physicochemical characteristics of the root canal dentin.

Conclusion

In conclusion, the use of root canal irrigants containing Im-AgNPs and ZnONPs nanoparticles can significantly improve the microhardness of the root canal dentin in the coronal (ZnONPs), middle, and apical thirds (Im-AgNPs).

Data Availability

The datasets used and/or analysed during the current study are available from the corresponding author on reasonable request.

Abbreviations

Zinc oxide:

ZnONPs

Silver:

AgNPs

Imidazolium-based silver:

Im-AgNPs

Vickers Hardness Number:

VHN

Sodium hypochlorite:

NaOCl

Ethylenediaminetetraacetic acid:

EDTA

Silver nitrate:

AgNPsNO3

Transmission electron microscopy:

TEM

X-ray diffraction spectroscopy:

XRD

Energy-dispersive X-ray spectroscopy:

EDS

Dimethylaminohexadecyl methacrylate:

DMAHDM

References

  1. Adl A, Razavian A, Eskandari F. The efficacy of EndoActivator, passive ultrasonic irrigation, and Ultra X in removing calcium hydroxide from root canals: an in-vitro study. BMC Oral Health. 2022;22(1):1–7.

    Google Scholar 

  2. Eskandari F, Abbaszadegan A, Gholami A, Ghahramani Y. The antimicrobial efficacy of graphene oxide, double antibiotic paste, and their combination against Enterococcus faecalis in the root canal treatment. BMC Oral Health. 2023;23(1):1–10.

    Google Scholar 

  3. Gonçalves LS, Rodrigues RCV, Junior CVA, Soares RG, Vettore MV. The effect of sodium hypochlorite and chlorhexidine as irrigant solutions for root canal disinfection: a systematic review of clinical trials. J Endod. 2016;42(4):527–32.

    PubMed  Google Scholar 

  4. Varshini R, Subha A, Prabhakar V, Mathini P, Narayanan S, Minu K. Antimicrobial efficacy of Aloe vera, lemon, Ricinus communis, and calcium hydroxide as intracanal medicament against Enterococcus faecalis: a confocal microscopic study. J Pharm Bioallied Sci. 2019;11(Suppl 2):256.

    Google Scholar 

  5. Chan EL, Zhang C, Cheung GS. Cytotoxicity of a novel nano-silver particle endodontic irrigant. Clin Cosmet Investig Dent. 2015;7:65–74.

    PubMed  PubMed Central  Google Scholar 

  6. Generali L, Bertoldi C, Bidossi A, Cassinelli C, Morra M, Del Fabbro M, et al. Evaluation of cytotoxicity and antibacterial activity of a new class of silver citrate-based compounds as endodontic irrigants. Materials. 2020;13(21):5019–33.

    PubMed  PubMed Central  Google Scholar 

  7. Patel E, Pradeep P, Kumar P, Choonara YE, Pillay V. Oroactive dental biomaterials and their use in endodontic therapy. J Biomed Mater Res B Appl Biomater. 2020;108(1):201–12.

    PubMed  Google Scholar 

  8. Mohammadi Z, Shalavi S, Moeintaghavi A, Jafarzadeh H. A review over benefits and drawbacks of combining sodium hypochlorite with other endodontic materials. The Open Dentistry Journal. 2017;11:661–9.

    PubMed  PubMed Central  Google Scholar 

  9. Gherasim O, Puiu RA, Bîrcă AC, Burdușel A-C, Grumezescu AM. An updated review on silver nanoparticles in biomedicine. Nanomaterials. 2020;10(11):2318–62.

    PubMed  PubMed Central  Google Scholar 

  10. Sahebi S, Asheghi B, Samadi Y, Eskandari F. Effect of Calcium Hydroxide and Nano Calcium Hydroxide on push-out bond strength of Epoxy Resin Sealer to Root Canal dentin. Iran Endod J. 2022;17(1):13–9.

    PubMed  PubMed Central  Google Scholar 

  11. Abootalebi SN, Mousavi SM, Hashemi SA, Shorafa E, Omidifar N, Gholami A. Antibacterial effects of green-synthesized silver nanoparticles using Ferula asafoetida against Acinetobacter baumannii isolated from the hospital environment and assessment of their cytotoxicity on the human cell lines. J Nanomater. 2021;2021:1–12.

    Google Scholar 

  12. Ebrahimi N, Rasoul-Amini S, Ebrahiminezhad A, Ghasemi Y, Gholami A, Seradj H. Comparative study on characteristics and cytotoxicity of bifunctional magnetic-silver nanostructures: synthesized using three different reducing agents. Acta Metall Sin (Engl Lett). 2016;29:326–34.

    Google Scholar 

  13. Gholami A, Mousavi SM, Shomali A, Hashemi SA, Abootalebi SN, Chiang W-H et al. One-put Ferula-mediated synthesis of Biogenic Silver Nanoparticles with more Antimicrobial Effect and Promising Human Cell Biocompatibility. J Nanomaterials. 2022.

  14. Loyola-Rodríguez JP, Torres-Méndez F, Espinosa-Cristobal LF, García-Cortes JO, Loyola-Leyva A, González FJ, et al. Antimicrobial activity of endodontic sealers and medications containing chitosan and silver nanoparticles against Enterococcus faecalis. J Appl Biomater Funct Mater. 2019;17(3):2280800019851771.

    PubMed  Google Scholar 

  15. Abbaszadegan A, Nabavizadeh M, Gholami A, Aleyasin Z, Dorostkar S, Saliminasab M, et al. Positively charged imidazolium-based ionic liquid‐protected silver nanoparticles: a promising disinfectant in root canal treatment. Int Endod J. 2015;48(8):790–800.

    PubMed  Google Scholar 

  16. Farshad M, Abbaszadegan A, Ghahramani Y, Jamshidzadeh A. Effect of imidazolium-based silver nanoparticles on root dentin roughness in comparison with three common root canal irrigants. Iran Endod J. 2017;12(1):83–6.

    PubMed  PubMed Central  Google Scholar 

  17. Nabavizadeh M, Ghahramani Y, Abbaszadegan A, Jamshidzadeh A, Jenabi P, Makarempour A. In vivo biocompatibility of an ionic liquid-protected silver nanoparticle solution as root canal irrigant. Iran Endod J. 2018;13(3):293–8.

    PubMed  PubMed Central  Google Scholar 

  18. Abbaszadegan A, Nabavizadeh M, Gholami A, Aleyasin Z, Dorostkar S, Saliminasab M et al. Positively charged imidazolium-based ionic liquid‐protected silver nanoparticles: a promising disinfectant in root canal treatment. 2015;48(8):790–800.

  19. Chávez-Andrade GM, Tanomaru-Filho M, Rodrigues EM, Gomes-Cornélio AL, Faria G, Bernardi MIB et al. Cytotoxicity, genotoxicity and antibacterial activity of poly (vinyl alcohol)-coated silver nanoparticles and farnesol as irrigating solutions. 2017;84:89–93.

  20. Farshad M, Abbaszadegan A, Ghahramani Y, Jamshidzadeh AJIej. Effect of imidazolium-based silver nanoparticles on root dentin roughness in comparison with three common root canal irrigants. 2017;12(1):83.

  21. Nabavizadeh M, Ghahramani Y, Abbaszadegan A, Jamshidzadeh A, Jenabi P. Makarempour AJIej. In vivo biocompatibility of an ionic liquid-protected silver nanoparticle solution as root canal irrigant. 2018;13(3):293.

  22. Eskandari F, Mofidi H, Asheghi B, Mohammadi F, Gholami A. Bringing resistance modulation to methicillin-resistant Staphylococcus aureus (MRSA) and vancomycin-resistant enterococci (VRE) strains using a quaternary ammonium compound coupled with zinc oxide nanoparticles. World J Microbiol Biotechnol. 2023;39(7):193.

    PubMed  Google Scholar 

  23. Jowkar Z, Fattah Z, Ghanbarian S, Shafiei F. The effects of silver, zinc oxide, and titanium dioxide nanoparticles used as dentin pretreatments on the microshear bond strength of a conventional glass ionomer cement to dentin. Int J Nanomed. 2020;15:4755–62.

    Google Scholar 

  24. Jowkar Z, Omidi Y, Shafiei F. The effect of silver nanoparticles, zinc oxide nanoparticles, and titanium dioxide nanoparticles on the push-out bond strength of fiber posts. J Clin Exp Dent. 2020;12(3):e249–e56.

    PubMed  PubMed Central  Google Scholar 

  25. Versiani MA, Abi Rached-Junior FJ, Kishen A, Pécora JD, Silva-Sousa YT, de Sousa-Neto MD. Zinc oxide nanoparticles enhance physicochemical characteristics of Grossman sealer. J Endod. 2016;42(12):1804–10.

    PubMed  Google Scholar 

  26. Jowkar Z, Hamidi SA, Shafiei F, Ghahramani Y. The effect of silver, zinc oxide, and titanium dioxide nanoparticles used as final irrigation solutions on the fracture resistance of root-filled teeth. Clin Cosmet Investig Dent. 2020;12:141–8.

    PubMed  PubMed Central  Google Scholar 

  27. Ari H, Erdemir A, Belli S. Evaluation of the effect of endodontic irrigation solutions on the microhardness and the roughness of root canal dentin. J Endod. 2004;30(11):792–5.

    PubMed  Google Scholar 

  28. Aslantas EE, Buzoglu HD, Altundasar E, Serper A. Effect of EDTA, sodium hypochlorite, and chlorhexidine gluconate with or without surface modifiers on dentin microhardness. J Endod. 2014;40(6):876–9.

    PubMed  Google Scholar 

  29. Oliveira LD, Carvalho CAT, Nunes W, Valera MC, Camargo CHR, Jorge AOC. Effects of chlorhexidine and sodium hypochlorite on the microhardness of root canal dentin. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 2007;104(4):e125–e8.

    PubMed  Google Scholar 

  30. Bakr DK, Saleem SS, Amin BK. Effect of sodium hypochlorite, chlorhexidin and EDTA on dentin microhardness. Zanco J Med Sci. 2016;20(1):11759–9.

    Google Scholar 

  31. Saha SG, Sharma V, Bharadwaj A, Shrivastava P, Saha MK, Dubey S, et al. Effectiveness of various endodontic irrigants on the micro-hardness of the root canal dentin: an in vitro study. J Clin Diagn Res. 2017;11(4):ZC01–ZC4.

    PubMed  PubMed Central  Google Scholar 

  32. Abbaszadegan A, Ghahramani Y, Gholami A, Hemmateenejad B, Dorostkar S, Nabavizadeh M, et al. The effect of charge at the surface of silver nanoparticles on antimicrobial activity against gram-positive and gram-negative bacteria: a preliminary study. J Nanomater. 2015;16(1):53.

    Google Scholar 

  33. Abbaszadegan A, Gholami A, Abbaszadegan S, Aleyasin ZS, Ghahramani Y, Dorostkar S, et al. The effects of different ionic liquid coatings and the length of alkyl chain on antimicrobial and cytotoxic properties of silver nanoparticles. Iran Endod J. 2017;12(4):481.

    PubMed  PubMed Central  Google Scholar 

  34. Gholami A, Ghezelbash K, Asheghi B, Abbaszadegan A, Amini A. An in vitro study on the antibacterial effects of chlorhexidine-loaded positively charged silver nanoparticles on Enterococcus faecalis. Journal of Nanomaterials. 2022;2022.

  35. Gholami A, Shams MS, Abbaszadegan A, Nabavizadeh M. Ionic liquids as capping agents of silver nanoparticles. Part II: antimicrobial and cytotoxic study. Green Process Synthesis. 2021;10(1):585–93.

    Google Scholar 

  36. Sahebi S, Sobhnamayan F, Moazami F, Naseri M. Assessment of sodium thiosulfate neutralizing effect on micro-hardness of dentin treated with sodium hypochlorite. BMC Oral Health. 2020;20(1):1–6.

    Google Scholar 

  37. Shameli K, Ahmad MB, Jazayeri SD, Shabanzadeh P, Sangpour P, Jahangirian H, et al. Investigation of antibacterial properties silver nanoparticles prepared via green method. Chem Cent J. 2012;6(1):1–10.

    Google Scholar 

  38. Shamhari NM, Wee BS, Chin SF, Kok KY. Synthesis and characterization of zinc oxide nanoparticles with small particle size distribution. Acta chimica Slovenica. 2018;65(3):578–85.

    PubMed  Google Scholar 

  39. Zak AK, Razali R, Abd Majid WH, Darroudi M. Synthesis and characterization of a narrow size distribution of zinc oxide nanoparticles. Int J Nanomed. 2011;6:1399–403.

    Google Scholar 

  40. Kalishwaralal K, Deepak V, Ramkumarpandian S, Nellaiah H, Sangiliyandi G. Extracellular biosynthesis of silver nanoparticles by the culture supernatant of Bacillus licheniformis. Mater Lett. 2008;62(29):4411–3.

    Google Scholar 

  41. Mehta B, Chhajlani M, Shrivastava B, editors. Green synthesis of silver nanoparticles and their characterization by XRD. Journal of physics: conference series; 2017: IOP Publishing.

  42. Sarkar R, Kumbhakar P, Mitra A. Green synthesis of silver nanoparticles and its optical properties. Dig J Nanomater Biostruct. 2010;5(2):491–6.

    Google Scholar 

  43. Lodhi FL, Saleem MI, Aqib AI, Rashid I, Qureshi ZI, Anwar MA, et al. Bringing resistance modulation to epidemic methicillin resistant S. aureus of dairy through antibiotics coupled metallic oxide nanoparticles. Microb Pathog. 2021;159:105138.

    PubMed  Google Scholar 

  44. Ballal NV, Mala K, Bhat KS. Evaluation of the effect of maleic acid and ethylenediaminetetraacetic acid on the microhardness and surface roughness of human root canal dentin. J Endod. 2010;36(8):1385–8.

    PubMed  Google Scholar 

  45. Mofidi H, Khosravani SR, Garjani S, Mirghotbi T. Evaluate the efficacy of laser therapy in root canal disinfection with different irrigants protocols: a systematic review and meta-analysis. Eurasia J Biosci. 2020;14:4697–701.

    Google Scholar 

  46. Sedigh-Shams M, Ebrahimi R, Asheghi B, Eskandari F. Comparative evaluation of cyclic fatigue resistance of two single-file rotary instruments in simulated stainless steel curved canals. J Res Dent Maxillofac Sci. 2022;7(1):48–54.

    Google Scholar 

  47. Elika V, Kunam D, Anumula L, kumar Chinni S, Govula K. Comparative evaluation of Chloroquick with Triphala, sodium hypochlorite, and ethylenediaminetetraacetic acid on the microhardness of root canal dentin: an in vitro study. J Clin Transl Res. 2021;7(1):72–6.

    PubMed  PubMed Central  Google Scholar 

  48. Arslan H, Barutcigil C, Karatas E, Topcuoglu HS, Yeter KY, Ersoy I, et al. Effect of citric acid irrigation on the fracture resistance of endodontically treated roots. Eur J dentistry. 2014;8(01):074–8.

    Google Scholar 

  49. Zhang Y-R, Du W, Zhou X-D, Yu H-Y. Review of research on the mechanical properties of the human tooth. Int J Oral Sci. 2014;6(2):61–9.

    PubMed  PubMed Central  Google Scholar 

  50. Ghisi AC, Kopper PMP, Baldasso FE, Stürmer CP, Rossi-Fedele G, Steier L, et al. Effect of super-oxidized water, sodium hypochlorite and EDTA on dentin microhardness. Braz Dent J. 2014;25:420–4.

    PubMed  Google Scholar 

  51. Pashley D, Okabe A, Parham P. The relationship between dentin microhardness and tubule density. Dent Traumatol. 1985;1(5):176–9.

    Google Scholar 

  52. Angker L, Nockolds C, Swain MV, Kilpatrick N. Correlating the mechanical properties to the mineral content of carious dentine—a comparative study using an ultra-micro indentation system (UMIS) and SEM-BSE signals. Arch Oral Biol. 2004;49(5):369–78.

    PubMed  Google Scholar 

  53. Saghiri MA, Delvarani A, Mehrvarzfar P, Malganji G, Lotfi M, Dadresanfar B, et al. A study of the relation between erosion and microhardness of root canal dentin. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 2009;108(6):e29–e34.

    PubMed  Google Scholar 

  54. Slutzky-Goldberg I, Maree M, Liberman R, Heling I. Effect of sodium hypochlorite on dentin microhardness. J Endod. 2004;30(12):880–2.

    PubMed  Google Scholar 

  55. Philip PM, Sindhu J, Poornima M, Naveen D, Nirupama D, Nainan MT. Effects of conventional and herbal irrigants on microhardness and flexural strength of root canal dentin: an in vitro study. J Conserv Dent. 2021;24(1):83–7.

    PubMed  PubMed Central  Google Scholar 

  56. Bosaid F, Aksel H, Makowka S, Azim A. Surface and structural changes in root dentine by various chelating solutions used in regenerative endodontics. Int Endod J. 2020;53(10):1438–45.

    PubMed  Google Scholar 

  57. Bhandi S, Mehta D, Mashyakhy M, Chohan H, Testarelli L, Thomas J, et al. Antimicrobial efficacy of silver nanoparticles as root canal irrigant’s: a systematic review. J Clin Med. 2021;10(6):1152.

    PubMed  PubMed Central  Google Scholar 

  58. Charannya S, Duraivel D, Padminee K, Poorni S, Nishanthine C, Srinivasan MR. Comparative evaluation of antimicrobial efficacy of silver nanoparticles and 2% chlorhexidine gluconate when used alone and in combination assessed using agar diffusion method: an in vitro study. Contemp Clin Dent. 2018;9(Suppl 2):204–S9.

    Google Scholar 

  59. Suzuki TYU, Gallego J, Assunção WG, Briso ALF, Dos Santos PH. Influence of silver nanoparticle solution on the mechanical properties of resin cements and intrarradicular dentin. PLoS ONE. 2019;14(6):e0217750.

    PubMed  PubMed Central  Google Scholar 

  60. Hassan R, Khallaf M. Effect of a silver nanoparticle intracanal-based medicament on the microhardness of human radicular dentine. Endod Pract Today. 2018;12:125–7.

    Google Scholar 

  61. Baras BH, Sun J, Melo MAS, Tay FR, Oates TW, Zhang K, et al. Novel root canal sealer with dimethylaminohexadecyl methacrylate, nano-silver and nano-calcium phosphate to kill bacteria inside root dentin and increase dentin hardness. Dent Mater. 2019;35(10):1479–89.

    PubMed  Google Scholar 

  62. Adl A, Abbaszadegan A, Gholami A, Parvizi F, Ghahramani Y. Effect of a new imidazolium-based silver nanoparticle irrigant on the bond strength of epoxy resin sealer to root canal dentine. Iran Endod J. 2019;14(2):122–5.

    PubMed  PubMed Central  Google Scholar 

  63. Patra JK, Baek K-H. Green nanobiotechnology: factors affecting synthesis and characterization techniques. J Nanomater. 2014;2014:1–13.

    Google Scholar 

  64. Zhu J, Liang R, Sun C, Xie L, Wang J, Leng D, et al. Effects of nanosilver and nanozinc incorporated mesoporous calcium-silicate nanoparticles on the mechanical properties of dentin. PLoS ONE. 2017;12(8):e0182583.

    PubMed  PubMed Central  Google Scholar 

  65. Al-Naimi RJ, Al-Alousi WS, Al-Nema M. Effect of silver and zinc oxide nanoparticle addition on microhardness and depth of cure of resin based pit and fissure sealants. Int J Enhanc Res Sci Technol Eng. 2015;4(4):157–63.

    Google Scholar 

Download references

Acknowledgements

This article was based on the postgraduate thesis by Dr. Hossein Mofid in partial fulfillment for the degree of Master of Science in Endodontics. Appreciation is expressed to Ms. Farzaneh Rasooli for copyediting, proofreading, and improving the use of English in this manuscript and Dr. Parisa Chamanpara for helping with the statistical analyses.

Funding

This study was founded by Vice-Chancellery of Shiraz University of Medical Sciences (Grant#23198). This fund was used for the collection of samples, providing the materials and tests, and statistical analysis of data.

Author information

Authors and Affiliations

  1. Department of Endodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Fars, Iran

    Safoora Sahebi & Abbas Abbaszadegan

  2. Endodontist, Department of Endodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran

    Hossein Mofidi

  3. Biotechnology Research Center, Shiraz University of Medical Sciences, Shiraz, Fars, Iran

    Ahmad Gholami

  4. Pharmaceutical Sciences Research Center, Shiraz University of Medical Sciences, Shiraz, Fars, Iran

    Ahmad Gholami

  5. Department of Pharmaceutical Biotechnology, School of Pharmacy, Shiraz University of Medical Sciences, Shiraz, Fars, Iran

    Ahmad Gholami

  6. School of Dentistry, Shiraz University of Medical Sciences, Ghasrdasht Street, Shiraz, 71956-15878, Iran

    Fateme Eskandari

Authors
  1. Safoora Sahebi
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Hossein Mofidi
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Abbas Abbaszadegan
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Ahmad Gholami
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Fateme Eskandari
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

“SS conceptualized, designed, and supervised the study, and edited the manuscript. HM performed the laboratory works and tests. AA conceptualized and designed the methodology. AG synthesized the materials and designed the methodology. FE was involved in data curation and formal analysis and was a major contributor in writing the manuscript. All authors read and approved the final manuscript.“

Corresponding authors

Correspondence to Ahmad Gholami or Fateme Eskandari.

Ethics declarations

Ethics approval and consent to participate

This study design was approved by the Ethics in Human Research Committee of Shiraz University of Medical Sciences (Ethics ID no. IR.SUMS.DENTAL.REC.1400.043). All human teeth used for this study were collected from the Oral and Maxillofacial Surgery Department of Shiraz dental school. These patients informed that their tooth will be used for research purposes and all of the patients or their parents signed a written informed consent form before the extraction of teeth. The study was performed in full accordance with ethical principles, including the World Medical Association Declaration of Helsinki (version 2008).

Consent for publication

Not applicable.

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sahebi, S., Mofidi, H., Abbaszadegan, A. et al. The effect of nanobased irrigants on the root canal dentin microhardness: an ex-vivo study. BMC Oral Health 23, 581 (2023). https://doi.org/10.1186/s12903-023-03298-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s12903-023-03298-z

Keywords

BMC Oral Health

ISSN: 1472-6831

Contact us