Force degradation of two orthodontic accessories analyzed in vivo and in vitro

BMC Oral Health volume 23, Article number: 1001 (2023) Cite this article

Abstract

Objective

To compare force degradation of elastomeric chains and NiTi coil springs in vivo and in vitro, and evaluate the effects of pre-stretched and reused elastomeric chains in the oral cavity during the time.

Methods

In the in vitro groups, 4-unit elastomeric chains and NiTi coil springs with an initial force of 200 g were placed in dry air and artificial saliva. The volunteers wore clear retainers which were used to hold the sample of 4-unit chains, pre-stretched 4-unit chains, and NiTi coil springs with the initial force of 200 g in the in vivo groups. After the first 4 weeks, 4-unit specimens were stretched to 200 g again for another 4 weeks in vivo. The force value and the percentage of force degradation were recorded at each measurement time interval in the in vivo and in vitro groups.

Results

The force degradation of elastomeric chains was greatest within the initial 4 hours, followed by a more stable phase after 1 week. The average force degradation of 4-unit elastomeric chains after 4 weeks was in vivo (64.8%) > artificial saliva (55.0%) > dry air (46.42%) (P < 0.05). The force degradation of NiTi coil springs in vivo (15.36%) or in artificial saliva (15.8%) was greater than in dry air (7.6%) (P < 0.05). NiTi coil springs presented a gentler force decay than elastomeric chains during the period (P < 0.05). In vivo, the force degradation of pre-stretched and reused elastomeric chains decreased less than the regular style(P < 0.05).

Conclusion

The force degradation of the elastomeric chains and NiTi coil springs varied in different environments. NiTi coil springs presented a gentler force decay than elastomeric chains during the period. Orthodontists should consider the force degradation characteristics of orthodontic accessories in clinical practice.

Peer Review reports

Introduction

Elastomeric chains were introduced to the dental profession in the 1960s [1]. Since then, they have been extensively used in orthodontics mainly for retracting canines and incisors after premolar extraction [2,3,4,5]. They were polymeric materials without ideal elasticity. One of the major characteristics of the elastomeric chains was that they absorbed saliva and experienced permanent deformation and force degradation in the oral environment due to the breakdown of internal bonds [6, 7].

Force degradation of elastomeric chains has been previously investigated in vitro studies [1, 3, 8,9,10,11,12,13,14,15,16]. Several studies have reported that the initial force of elastomeric chains slumped on the first day of use and kept this momentum. This variation range depends on several factors including the chain composition, environment, evaluation method, pre-stretched treatment, and initial force applied [8, 9].

Nickel titanium (NiTi) coil springs are also commonly used in space-closing systems. They are metallic materials with the unique property of super-elasticity. Compared to elastomeric chains, the force value of NiTi coil springs remained relatively constant during the period [14, 17, 18]. Since sliding mechanics have been widely applied to close residual extraction spaces, it is important to compare the force exerted by elastomeric chains and NiTi coil springs to assist orthodontists in selecting the appropriate devices.

In vitro studies simplified the system, allowing investigators to focus on a small number of factors and exclude some variables [15]. Despite the advantages of in vitro experiments, laboratory conditions cannot exactly simulate the real oral cavity. The oral environment of orthodontic patients seemed to be ideal for analyzing the characteristics of elastomeric chains and NiTi coil springs currently used under load. However, it was difficult to systematically assess the individual responses to the same orthodontic force and to standardize the distance or initial force. In vivo studies could better evaluate the factors affecting the force degradation of elastomeric chains and provide more reliable guidance for clinical applications of elastic force. Therefore, it is necessary to evaluate the characteristics of elastomeric chains and NiTi coil springs with the standardization both in vitro and in vivo.

The aim of this study was to evaluate the characteristics of force degradation of the two orthodontic accessories. This study tested the hypothesis that there would be a difference in force degradation between two orthodontic accessories and the force would decay differently in different environments.

Materials and methods

Elastomeric chains (AlastiK transparent Spool Chain, 3 M Uniteck, USA) and NiTi coil springs (A-W-CS10506D, IMD, China) were used in the in vivo and in vitro experiments. Eighty pieces of 4-unit elastomeric chains and 60 NiTi coil springs were divided into 8 groups according to different environments and treatments, each with 20 samples (Table 1).

Table 1 Groups of two orthodontic accessories in different environments and treatments
Full size table

The force values of the stretched samples were measured in a testing machine (load sensor 500G/5N, accuracy of 0.01 mm; Dongguan ZHIQU company, Dongguan, China) (Fig. 1A). Tensile readings were recorded in gram (g) force with a duration of 10 seconds for each sample. The length of the setting force (200 g) was measured for each group by electronic digital display Vernier (accuracy of 0.01 mm; Germany Master proof Company, Shanghai, China). Two hooks made of 1 mm stainless steel were used to hold each side of the specimens on the screws of the base (Fig. 1A). Then the average length of each group was the extension distance. All groups were extended to a specific distance using the same initial force of about 200 g and measured at intervals of initial, 4 hours, 1 day, 4 days, 1 week, 2 weeks, 3 weeks, and 4 weeks. These measurements were conducted by one investigator (L.Y) to ensure consistent handling of the test machine. With a pair of tweezers, each tested specimen was carefully removed from the retainer and transferred to the testing machine in the sequence of time intervals. In the process of stretching from a relaxed state to a specific distance, the force value of elastomeric chains, as shown on the test machine, gradually increased. When the specimen was stretched to a specific distance, the force value decreased rapidly at first, and then it tended to decline stably. The force value of the specimen was determined by taking the constant value of the test machine within 10 seconds, and each specimen was read three times for the average force value.

Fig. 1
figure 1

A Elastomeric chains tested by the testing machine. Detail of two hooks coupled to the testing machine, one was at its upper connection point and the other was fixed at the bottom. A diagram of the stretched elastomeric chains inserted on hooks. NiTi coil springs were tested using the same way. B Insertion of elastomeric chains and NiTi coil springs on buttons maintained by clear retains. L represented the distance of extension (mm)

Full size image

For the in vivo experiment, ten college students were chosen to wear clear retainers as volunteers from the School of Stomatology, Zhejiang Chinese Medical University. The inclusion and exclusion criteria for the volunteers were as follows: good physical and mental health, regular lifestyle, no history of orthodontic treatment, no bruxism, no dental crowding, and no moderate or severe periodontal disease. All participating subjects had signed an informed consent agreement. Silicon rubber impressions were collected to produce gypsum models of the maxillary and mandibular arches for each individual. A vacuum pressure film machine (Guang Ming Medical Device Company, Suzhou, China) was used to customize thermoplastic retainers of upper and lower arches. Light solidification glue was used to fix two buttons (diameter = 1 mm) on each quadrant of the clear retainers, representing the distance of Group I-IV extension to produce an initial force value (200 g). After the first 4 weeks, the elastomeric chains in Group I were removed from the clear retainers of different volunteers, and then the position of two buttons on the clear retainer was adjusted to represent the distance of reused elastomeric chains in Group IV. To prevent the elastomeric chains from breaking, volunteers had to wear clear retainers except for three basic meals all day, except during three main meals, and to avoid consuming any other beverages (Fig. 1B).

For the in vitro experiment, 4-unit elastomeric chains and NiTi coil springs were stretched to the setting force in retainers, as previously done. Instead of being worn in volunteers’ mouths, retainers were placed in a dry environment with a constant temperature of 25 °C and relative humidity of 60%. They were also immersed in artificial saliva with a constant temperature of 37 °C and a pH of 6.7. The artificial saliva, which closely resembles natural saliva, consists of the following components: KCl (0.4 g/L), NaCl (0.4 g/L), CaCl2·2H2O (0.906 g/L), NaH2PO4·2H2O (0.690 g/L), Na2S·9H2O (0.005 g/L), and Urea (1 g/L). The solution was titrated to a pH of 6.7 using NaOH (5 mol/L) and replaced once a week. Force measurements were made at the same time intervals as the in vivo experiments.

Statistical analysis

The collected data was analyzed by the SPSS software (Version 22.0, IBM, Armonk, NY). The means and standard deviations of force degradation were calculated for each group at each time interval. One-way ANOVA test with Bonferroni correction and t-test were used to identify statistically significant intragroup and intergroup differences at a 5% significance level.

Result

The means and standard deviation of the force value and the force degradation percentage of all groups at each measured time interval were shown in Table 2. The curve extension of elastomeric chains in different environments showed a decreasing trend of force value over time. Within the initial 4 hours, the degradation of the elastic force was the greatest, the average degradation rate of the elastic force was as follows: in vivo (35.9%) > artificial saliva (29.1%) > dry air condition (14.9%) (P < 0.05). After that, the degradation of force value decreased steadily. After 4 weeks, the average degradation of the 4-unit elastomeric chains force were as follows: in vivo (64.8%) > artificial saliva (55.0%) > dry air condition (46.4%) (P < 0.05) (Fig. 2A). At the same time point, the force degradation of NiTi coil springs decreased more obviously in vivo and in artificial saliva compared with the dry air condition (P < 0.05). However, there were no statistically significant differences between the in vivo and artificial saliva groups. After 4 weeks, the force degradation of NiTi coil springs was 15.2% in vivo, 15.1% in artificial saliva, and 7.6% in the dry air (Fig. 2B).

Table 2 Means and standard deviations of the extension force (g) and percentage of force degradation (%) for each group
Full size table
Fig. 2
figure 2

Force degradation (%) over time of elastomeric chains and NiTi coil springs groups. A * Denotes statistically significant differences among three groups at the same time point. B * Denotes statistically significant differences between group VI and group II or group VIII at the same time point. C * Denotes statistically significant differences between group I and group III or group IV at the same time point

Full size image

For the in vivo groups, the force degradation of elastomeric chains and NiTi coil springs were compared. Under the same force value (200 g), elastomeric chains showed a significantly higher degradation rate than NiTi coil springs at all time intervals (P < 0.05). After 4 weeks, the degradation of elastomeric chains was about 4 times higher than that of NiTi coil springs.

Degradation of the elastic force was compared under the same situation but with different treatments. In vivo, pre-stretched 4-unit elastomeric chains (Group III) and reused 4-unit elastomeric chains (Group IV) showed less force degradation than untreated elastomeric chains (Group I) at all time intervals (P < 0.05). After 4 weeks, the force degradation rate of Group III was 51.1% and Group IV was 48.4%, both of which were less than that of Group I (64.8%) (Fig. 2C).

Discussion

This study was conducted to test the hypothesis that there would be a difference in force degradation between two accessories and among different environments. The initial force of all groups was standardized at 200 g in this study, as it lay within the optimal force magnitude for space closure and could be considered equal for evaluating the force degradation. Two orthodontic accessories were fixed between the button points correspondingly in the personalized retainer to prevent direct force application to the teeth. In this way, the actual dynamic situation of orthodontic treatment could be simulated, especially for space closure.

The present study found that the force degradation of elastomeric chains in vivo (64.8%) was greater than in dry air (46.4%) and in artificial saliva (55.0%) after 4 weeks, which seemed to be a similar trend to those from previous in vitro studies [3, 10,11,12, 15, 16, 19]. The percentage of force degradation varies among studies because of differences in the composition and size of elastomeric chains. Furthermore, consistent with findings from previous studies [10, 11, 15, 16, 19, 20], elastic force experienced the most significant degradation within the initial 4 hours, followed by a stable phase after 7 days. A recent report [21], using the same method to evaluate the properties of latex chains in vivo and in vitro, found that the force value of latex chains decreased faster in vivo than in vitro and exhibited a high percentage of force loss at the early stages. The latex chains and elastomeric chains were found to exhibit similar patterns of force degradation. One possible explanation for this similarity is that both materials are made of polyurethane, which lacks ideal elasticity and is sensitive to prolonged exposure to intraoral conditions. Considering the degradation regulations of elastomeric products, a slightly higher initial force value might be appropriate for clinical applications [4, 22, 23].

In this study, the force degradation of NiTi coil springs in dry air (7.6%) is relatively less than in vivo (15.2%) or artificial saliva (15.0%), which was similar to previous studies [17, 18, 24]. The reason was that the NiTi coil spring with shape memory could be less influenced by the humidity and pH of the environment [25]. Notably, compared with elastomeric chains, NiTi coil springs were more resistant to force degradation and presented a gentler and more progressive force degradation. After 4 weeks, the elastomeric chains showed a significantly greater force decay (64.8%) than that presented by the NiTi coil springs (15.2%), corroborating the results of other investigations [26]. Compared to elastomeric chains, NiTi materials with super-elasticity are supposed to overcome the issue of rapid force decay and provide light and continuous forces over a wide range of activation [24, 25]. However, they could easily accumulate food particles, which were difficult to remove and might be detrimental to oral hygiene. Thus, elastomeric chains remain popular in clinical practice due to their affordability, practicality, and ease of cleaning. Additionally, in space closure systems, elastomeric chains were considered to deliver intermittent forces that can provide time for alveolar bone remodeling and reduce side effects such as root resorption [23]. It is imperative for clinicians to be aware of the characteristics of the force delivery system to facilitate optimal selection.

To counteract the rapid loss of force of elastomeric chains, pre-stretching the elastomeric chain has been suggested to reduce force decay before it is stretched with tension [3, 22]. After the pre-stretching treatment, the elastomeric chains experience deformation, leading to an increased length after the post-stretching process. In clinical practice, for instance, elastomeric chains that initially required 5 units are now relieved by only 4 units to generate the same initial force value. The present study chose a method of pre-stretching treatment that was applicable at the chairside and compared its effect on the behavior of elastomeric chains with the same unit and initial force value. The extension distance of the pre-stretched group differs from that of the non-pre-stretched group to achieve the same initial force. This contrasts with some studies that used a uniform stretching distance like 30 mm [3], which could lead to different initial forces. It was found that with the same initial force (200 g), the force degradation of the pre-stretched groups was smaller than that of the non-pre-stretched groups after 4 weeks. These findings were in agreement with the results of Chang et al. [27], who also found that pre-stretching treatment was not accompanied by disadvantages such as permanent deformation. Whether the pre-stretching treatment of elastomeric chains with different units or different initial force values will affect the force degradation of elastomeric chains needs further study.

Since there was a loss of force over time, clinicians conventionally removed the original chains and replaced them with new chains in a patient’s mouth every 4 to 6 weeks. It is unknown whether the original chains that were reused and stretched again have the same mechanical performance as the non-reused ones [28]. In Group IV, 4-unit elastomeric chains tested in Group I after 4 weeks were reused in vivo. In the same situation, the results showed that the force degradation of Group IV was less than non-reused elastomeric chains at all time intervals (P < 0.05). In this experiment, volunteers were asked to wear the retainers except during meals. This approach helped to eliminate various factors that could potentially affect the results, such as the patient’s diet, masticatory force, tooth-brushing, the presence of bacterial enzymes, and temperature changes. All the above factors could lead to permanent deformation and increase the force degradation of elastomeric chains. Hence, the treatment of reused elastomeric chains should be chosen based on the actual situation.

This study had several limitations. The extension distance of orthodontic accessories might decrease during the process of tooth space closure, whereas the extension distance remained constant in our study. Consequently, the force degradation of two orthodontic accessories might be influenced by changes in distance. Although volunteers were required to wear clear retainers for about 22 hours a day, the wear time of the elastomeric chains was less than that of the actual clinical situation (24 hours a day). Therefore, the in vivo group was unable to fully replicate the actual situation of orthodontic therapy. Considering that, the force degradation of elastomeric chains in clinical practice might be greater than the results of our in vivo study.

Conclusion

  1. 1.

    The force degradation of the elastomeric chains and NiTi coil springs varied in different environments. NiTi coil springs presented a gentler force decay than elastomeric chains during the period.

  2. 2.

    Using pre-stretched and reused elastomeric chains might decrease the rate of force degradation.

  3. 3.

    In clinical practice, orthodontists should consider the force degradation characteristics of two orthodontic accessories when using them for space closure.

Availability of data and materials

All data generated or analyzed during this study are included in this published article.

References

  1. Eliades T, Eliades G, Silikas N, Watts DC. Tensimle properties of orthodontic elastomeric chains. Eur J Orthod. 2004;26(2):157–62.

    Article  PubMed  Google Scholar 

  2. Zhang C, Wen X, Vyavahare NR, Boland T. Synthesis and characterization of biodegradable electrometric polyurethane scaffolds fabricated by the inkjet technique. Biomaterials. 2008;29(28):3781–91.

    Article  PubMed  Google Scholar 

  3. Kim KH, Chung CH, Choy K, Lee JS, Vanarsdall RL. Effects of pre-stretching on force degradation of synthetic elastomeric chains. Am J Orthod Dentofac Orthop. 2005;128(4):477–82.

    Article  Google Scholar 

  4. Nightingale C, Jones SP. A clinical investigation of force delivery system for orthodontic space closure. Am J Orthod Dentofac Orthop. 2003;30(3):229–36.

    Google Scholar 

  5. Chimenti C, Lecce D, Santucci L, et al. In vitro assessment of elastomeric chain behavior. Prog Orthod. 2010;2(1):42–5.

    Article  Google Scholar 

  6. Rock WP, Wilson HJ, Fisher SE. A laboratory investigation of orthodontic elastomeric chains. Br J Orthod. 1985;12(4):202–7.

    Article  PubMed  Google Scholar 

  7. De Genova DC, McInnes Ledoux P, Wein-berg R, Shaye R. Force degradation of orthodontic elastomeric chains--a product comparison study. Am J Orthod Dentofac Orthop. 1985;87(5):377–84.

    Article  Google Scholar 

  8. Carolina B, Trindade MC, Matheus AJ, et al. In situ evaluation of orthodontic elastomeric chains. Braz Dent J. 2012;23(4):394–8.

    Article  Google Scholar 

  9. Yagura D, Baggio PE, Carreiro LS, et al. Deformation of elastomeric chains related to the amount and time of stretching. Dental Press J Orthod. 2013;18(3):136–42.

    Article  PubMed  Google Scholar 

  10. Balhoff DA, Shuldberg M, Hagan JL, et al. Force decay of elastomeric chains - a mechanical design and product comparison study. Br J Orthod. 2011;38(1):40–7.

    Article  Google Scholar 

  11. Buchmann N, Senn C, Ball J, Brauchli L. Influence of initial strain on the forece decay of currently available elastic chains over time. Angle Orthod. 2012;82(1):529–35.

    Article  PubMed  Google Scholar 

  12. Kochenborger C, Silva DL, Marchioro EM, Vargas DA, Hahn L. Assessment of force decay in orthodontic elastomeric chains: an in vitro study. Dental press. J Orthod. 2011;16(6):93–9.

    Google Scholar 

  13. Mirhashemi A, Saffarshahroudi A, Sodagar A, et al. Force degradation pattern of six different orthodontic elastomeric chains. J Dent. 2012;9(4):204–15.

    Google Scholar 

  14. Santos AC, Tortamano A, Naccarato SR, Dominguez-Rodriguez GC, Vigorito JW. An in vitro comparison of the force decay generated by different commercially available elastomeric chains and NiTi closed coil springs. Braz Oral Res. 2007;21(1):51–7.

    Article  PubMed  Google Scholar 

  15. Andre W, Arno L, De MLM, et al. In vitro evaluation of force degradation of elastomeric chains used in orthodontics. Dental Press J Orthod. 2013;18(1):55–62.

    Article  Google Scholar 

  16. Sang T, Wu J. Factors on force degradation of elastomeric chains in vitro. Shanghai J Stomato. 2008;17(6):638–42.

    Google Scholar 

  17. Tripolt H, Burstone CJ, Bantleon P, et al. Force characteristics of nickel-titanium tension coil springs. Am J Orthod Dentofac Orthop. 1999;115(5):498–507.

    Article  Google Scholar 

  18. Cox C, Nguyen T, Koroluk L, et al. In-vivo force decay of nickel-titanium closed-coil springs. Am J Orthod Dentofac Orthop. 2014;145(4):505–13.

    Article  Google Scholar 

  19. Halimi A, Azeroual MF, Doukkali A, et al. Elastomeric chain force decay in artificial saliva: an in vitro study. Int Orthod. 2013;11(1):60–70.

    PubMed  Google Scholar 

  20. JAJ B, Tuesta O. Flores-Mir C: in vivo comparison of force decay between injection molded and die-cut stamped elastomers. Am J Orthod Dentofac Orthop. 2006;129(3):384–9.

    Article  Google Scholar 

  21. Yang L, Lv C, Feng J, et al. Force degradation of orthodontic latex elastics analyzed in vivo and in vitro. Am J Orthod Dentofac Orthop. 2020;157(3):313–9.

    Article  Google Scholar 

  22. Ren Y, Maltha JC, Kuijpers-Jagtman AM. Optimum force magnitude for orthodontic tooth movement: a systematic literature review. Angle Orthod. 2003;73(1):86–92.

    PubMed  Google Scholar 

  23. Konoo T, Kim YJ, Gu GM, et al: Intermittent force in orthodontic tooth Movement.J Dent Res 2001, 80(2):457-460.

    Google Scholar 

  24. Mohammed H, Rizk MZ, Wafaie K, et al. Effectiveness of nickel-titanium springs vs elastomeric chains in orthodontic space closure: a systematic review and meta-analysis. Orthod Craniofacial Res. 2018;21(1):12–9.

    Article  Google Scholar 

  25. Espinar Escalona E, Llamas Carreras JM, Barrera Mora JM, et al. Effect of temperature on the orthodontic clinical applications of NiTi closed-coil springs. Med Oral Cir Bucal. 2013;18(4):721–4.

    Article  Google Scholar 

  26. Ubirajara Pires B, Rafael EDS, Vedovello Filho M, et al. Force degradation of different elastomeric chains and nickel titanium closed springs. Braz J Oral Sci. 2012;10(3):167–70.

    Google Scholar 

  27. Chang JH, Hwang CJ, Kim KH, et al. Effects of prestretching on stress relaxation and permanent deformation of orthodontic synthetic elastomeric chains. Korean. J Orthod. 2018;48(6):384–94.

    Google Scholar 

  28. Evans KS, Wood CM, Moffitt AH, et al. Sixteen-week analysis of unaltered elastomeric chain relating in-vitro force degradation with in-vivo extraction space tooth movement. Am J Orthod Dentofac Orthop. 2017;151(4):727–34.

    Article  Google Scholar 

Download references

Acknowledgements

We thank all volunteers who participated in the study for their cooperation and enthusiasm in wearing clear retainers for such a long time.

Funding

Not applicable

Author information

Author notes

  1. Liu Yang and Chenxing Lv are joint first authors and contributed equally to this work.

Authors and Affiliations

  1. Department of Stomatology, Hangzhou Traditional Chinese Medicine Hospital Affiliated to Zhejiang Chinese Medical University, Hangzhou, China

    Liu Yang

  2. Department of Orthodontics, State Key Laboratory of Oral and Maxillofacial Reconstruction and Regeneration, Key Laboratory of Oral Biomedicine Ministry of Education, Hubei Key Laboratory of Stomatology, School and Hospital of Stomatology, Wuhan University, Wuhan, China

    Chenxing Lv

  3. School and Hospital of Stomatology, Zhejiang Chinese Medical University, Hangzhou, China

    Xiaomin Li & Jianying Feng

Authors
  1. Liu Yang
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Chenxing Lv
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Xiaomin Li
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Jianying Feng
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

Conceived and designed the experiments: Jianying Feng Performed and experiments: Liu Yang, Chenxing Lv Analyzed the data: Liu Yang, Xiaomin Li Wrote the manuscript: Liu Yang, Chenxing Lv.

Corresponding author

Correspondence to Jianying Feng.

Ethics declarations

Ethics approval and consent to participate

The experimental protocol was established according to the ethical guidelines of the Helsinki Declaration and was approved by the Human Ethics Committee of Zhejiang Chinese Medical University. Written informed consent was obtained from individual or guardian participants.

Consent for publication

Not applicable

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Yang, L., Lv, C., Li, X. et al. Force degradation of two orthodontic accessories analyzed in vivo and in vitro. BMC Oral Health 23, 1001 (2023). https://doi.org/10.1186/s12903-023-03737-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s12903-023-03737-x

Keywords

BMC Oral Health

ISSN: 1472-6831

Contact us